Knowde Enhanced TDS
Identification & Functionality
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Applications
- Cure Method
- Recommendation for Laminating
Parts by weight:
Ocpol 800 VE 100 Cobalt 1% 0.6 gm DMA 0.1 gm Catalyst K 10 1.25 gm - Applications
- To start the curing reaction, take 100 parts of resin.
- Catalyst K 10 should be added to the resin system shortly before application to initiate the polymerization reaction.
- It is important to add the catalyst in carefully measured amounts to control the polymerization. Too much catalyst will cause too rapid a gelation time, whereas too little catalyst will result in under cure.
- Care must be taken to avoid explosive violence. Do not mix catalyst and cobalt octate or any accelerator together.
Properties
- Physical Form
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Viscosity at 25°C | 450 - 550 | cps | Brookfield LVT sp. 3@60 rpm |
| Gel Time at 25°C | 30 – 50 | min | — |
| Acid value | max. 14 | mg KOH/g | — |
| Solid content | 55±2 | % | — |
| Specific Gravity at 25°C | 1.10 – 1.11 | — | — |
| Peak Temperature | max. 170 | — | — |
| Barcol hardness (Model GYZJ 934 – 1) | 34 | — | — |
| Tensile Elongation | 5.2 | % | — |
| Tensile Strength | 85 | MPa | — |
| Tensile Modulus | 3.2 | GPa | — |
| Flexural Strength | 150 | MPa | — |
| Flexural Modulus | 3.7 | GPa | — |
| Heat Distortion Temperature | 111 | °C | — |
Safety & Health
- Safety
Due attention should be given to the precautions for handling chemicals provided in our Material Safety Data Sheet.
Packaging & Availability
- Packaging Type
- Packing
Ocpol 800 VE is supplied in 220 Kg new steel drums with close top.