Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Applications
- Applications
- Ideal to fill gaps up to 0.15mm
- Withstands working temperatures up to 300°F
- Used for rotors, shaft and gears in electric motors, bearings, and sleeves
- Excellent retaining and sealing compound
- Application Method
- Surfaces should be dry, clean, and free of any contamination. For best results, clean with a solvent and allow solvent to evaporate.
- If the material is an inactive metal or the cure speed is too slow, spray surfaces with our Turbo-Lock Primer/Activator and allow to dry.
- For Slip Fitted Assembles : Apply adhesive around the leading edge of the pin and the inside of the collar and use a rotating motion during assembly to ensure good coverage.
- For Press Slip Assemblies : Apply adhesive thoroughly to both bond surfaces and assemble at high press on rates.
- For Shrink Fitted Assemblies : The adhesive should be coated onto the pin, the collar should then be heated to create sufficient clearance for free assembly.
- For Disassembly : Apply localized heat to the assembly to approximately 250°C. Disassemble while hot.
Properties
- Color
- Physical Properties
- Typical Properties
- Chemical Resistance
- Cured Properties
- Adhesive Properties
| Value | Units | Test Method / Conditions | |
| Coefficient of Thermal Expansion | 80x10⁻⁶ | K-1 | ASTM D 696 |
| Coefficient of Thermal Conductivity | 0.1 | W/(m.K) | ASTM C 177 |
| Specific Heat | 0.3 | kJ/(kg.K) | — |
| Value | Units | Test Method / Conditions | |
| Average Strength (Steel) | 31.0 | N/mm² | — |
| Loctite® Equivalent | 638.0 | — | — |
| Permabond® Equivalent | A1046 | — | — |
| Value | Units | Test Method / Conditions | |
| Initial Strength Retained for Acetone (at 22ºC, 500hrs) | 100 | % | — |
| Initial Strength Retained for Ethanol (at 22ºC, 500hrs) | 100 | % | — |
| Initial Strength Retained for Motor Oil (at 125ºC, 500hrs) | 100 | % | — |
| Initial Strength Retained for Gasoline (at 22ºC, 500hrs) | 100 | % | — |
| Initial Strength Retained for Brake Fluid (at 22ºC, 500hrs) | 100 | % | — |
| Initial Strength Retained for Water/Glycol (at 87ºC, 500hrs) | 100 | % | — |
| Initial Strength Retained for Acetone (at 22ºC, 1000hrs) | 100 | % | — |
| Initial Strength Retained for Ethanol (at 22ºC, 1000hrs) | 100 | % | — |
| Initial Strength Retained for Motor Oil (at 125ºC, 1000hrs) | 100 | % | — |
| Initial Strength Retained for Gasoline (at 22ºC, 1000hrs) | 100 | % | — |
| Initial Strength Retained for Brake Fluid (at 22ºC, 1000hrs) | 100 | % | — |
| Initial Strength Retained for Water/Glycol (at 87ºC, 1000hrs) | 95 | % | — |
| Value | Units | Test Method / Conditions | |
| Handling Cure Time | 5 | minutes | — |
| Functional Cure Time | 1 - 3 | hrs | — |
| Full Cure Time | 24 | hrs | — |
| Compressive Shear Strength of Steel Pins and Collars (After 24 hrs, at 22ºC) | min. 27 (min. 3,500) | N/mm² (psi) | ISO 10123 |
| Compressive Shear Strength of Steel Pins and Collars (After 30 min, at 22ºC) | min. 15 (2100) | N/mm² (psi) | ISO 10123 |
| Temperature Range | -55 to 150 | ºF | — |
| Value | Units | Test Method / Conditions | |
| Color | Green | — | — |
| Composition | Methacrylate esters | — | — |
| Viscosity (at 20 rpm, 25ºC, Brookfield RVT Spindle 3) | 500 | cPs | — |
| Specific Gravity (at 25ºC) | 1.13 | — | — |
| Maximum Diameter of Thread/Gap Filling | 0.15 | mm | — |
| Flash Point | min. 100 | ºC | — |
| Solvent Content | None | — | — |
Safety & Health
- Precautions
This product and the auxiliary materials normally combined with it are capable of producing adverse health effects ranging from minor skin irritation to serious systemic effects. None of these materials should be used, stored, or transported until the handling precautions and recommendations as stated in the Material Safety Data Sheets (MSDS).
Storage & Handling
- Shelf Life
- 1 Year
- Storage Information
Anaerobic adhesives are ideally stored in a cool, dry place in unopened containers at a room temperature between 46°F to 82°F. Please do not return unused material to its original container.