Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Applications
- Applications
- Ideal for thread locking plated parts, vibration or moving components
- Ideal for fasteners between up to ¾” (up to 20 mm) diameters
- Locks and seals threaded joints-nuts, screws, and studs
- Meets 90% of all nut and bolt thread locking applications
- Meets Military specifications : MIL-S-46163
- Application Method
Surfaces should be dry, clean, and free of any contamination. Thread locker should be applied to the bolt in sufficient quantity to fill threads. Turbo-Lock 11 Series performs the best in thin bond gaps. This thread locker is specifically formulated to give controlled friction and torque/tension ratio during assembly.
Properties
- Color
- Physical Properties
- Typical Properties
- Chemical Resistance
- Cured Properties
- Adhesive Properties
| Value | Units | Test Method / Conditions | |
| Coefficient of Thermal Expansion | 80x10⁻⁶ | K-1 | ASTM D 696 |
| Coefficient of Thermal Conductivity | 0.1 | W/(m.K) | ASTM C 177 |
| Specific Heat | 0.3 | kJ/(kg.K) | — |
| Value | Units | Test Method / Conditions | |
| Loctite® Equivalent | 242.0 | — | — |
| Permabond® Equivalent | MM115 | — | — |
| Value | Units | Test Method / Conditions | |
| Initial Strength Retained for Acetone (at 22ºC, 500hrs) | 100 | % | — |
| Initial Strength Retained for Ethanol (at 22ºC, 500hrs) | 100 | % | — |
| Initial Strength Retained for Motor Oil (at 125ºC, 500hrs) | 100 | % | — |
| Initial Strength Retained for Gasoline (at 22ºC, 500hrs) | 100 | % | — |
| Initial Strength Retained for Brake Fluid (at 22ºC, 500hrs) | 100 | % | — |
| Initial Strength Retained for Water/Glycol (at 87ºC, 500hrs) | 90 | % | — |
| Initial Strength Retained for Acetone (at 22ºC, 1000hrs) | 80 | % | — |
| Initial Strength Retained for Ethanol (at 22ºC, 1000hrs) | 100 | % | — |
| Initial Strength Retained for Motor Oil (at 125ºC, 1000hrs) | 100 | % | — |
| Initial Strength Retained for Gasoline (at 22ºC, 1000hrs) | 100 | % | — |
| Initial Strength Retained for Brake Fluid (at 22ºC, 1000hrs) | 100 | % | — |
| Initial Strength Retained for Water/Glycol (at 87ºC, 1000hrs) | 85 | % | — |
| Value | Units | Test Method / Conditions | |
| Handling Cure Time | 10 | minutes | — |
| Functional Cure Time | 1 - 3 | hrs | — |
| Full Cure Time | 24 | hrs | — |
| Breakaway Torque (3/8 x 16 Steel Nuts and Bolts) | 8 - 17 (70 - 150) | N.m (lbs.in) | ISO 10964 |
| Breakaway Torque (3/8 x 16 Cadmium Nuts and Bolts) | 1 - 17 (10 - 60) | N.m (lbs.in) | ISO 10964 |
| Breakaway Torque (3/8 x 16 Zinc Nuts and Bolts) | 2 - 17 (20 - 60) | N.m (lbs.in) | ISO 10964 |
| Breakaway Torque (M10 Black Oxide Steel Nuts and Bolts) | 8 - 19 (71 - 168) | N.m (lbs.in) | ISO 10964 |
| Prevail Torque (3/8 x 16 Steel Nuts and Bolts) | 3 - 7 (25 - 60) | N.m (lbs.in) | ISO 10964 |
| Prevail Torque (3/8 x 16 Cadmium Nuts and Bolts) | 1 - 5 (4 - 40) | N.m (lbs.in) | ISO 10964 |
| Prevail Torque (3/8 x 16 Zinc Nuts and Bolts) | 1 - 4 (10 - 40) | N.m (lbs.in) | ISO 10964 |
| Temperature Range | -55 to 150 | ºC | — |
| Value | Units | Test Method / Conditions | |
| Color | Purple | — | — |
| Composition | Methacrylate ester | — | — |
| Viscosity (at 20 rpm, 25ºC, Brookfield RVT Spindle 3) | 1200 | cPs | — |
| Specific Gravity | 1.07 | — | — |
| Maximum Screw Size | ¾ (20) | inches (mm) | — |
| Flash Point | min. 100 | ºC | — |
Regulatory & Compliance
- Quality Standards
Safety & Health
- Precautions
This product and the auxiliary materials normally combined with it are capable of producing adverse health effects ranging from minor skin irritation to serious systemic effects. None of these materials should be used, stored, or transported until the handling precautions and recommendations as stated in the Material Safety Data Sheets (MSDS).
Storage & Handling
- Shelf Life
- 2 Years
- Storage Information
Anaerobic adhesives are ideally stored in a cool, dry place in unopened containers at a room temperature between 46°F to 82°F. Please do not return unused material to its original container.