Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Penetrates threads by capillary action. Medium strength thread-locker.
- Ideal for sealing hairline cracks, small nuts and bolts.
- Seals and welds porous metal parts. Localize heating and hand tools are needed for disassembly. Prevents corrosion and leakage.
- Secure setscrews and other assemblies after settings are completed.
- Fasteners on vibrating machines or moving components.
- Meets Military specifications: MIL-S-46163A Type III Grade R and MIL-S-22473 Letter Grade AA
- Application Method
Surfaces should be dry, clean, and free of any contamination. Thread locker should be applied to the bolt in sufficient quantity to fill threads. This thread locker is specifically formulated to give controlled friction and torque/tension ratio during assembly.
Properties
- Color
- Physical Properties
- Typical Properties
- Chemical Resistance
- Cured Properties
- Adhesive Properties
| Value | Units | Test Method / Conditions | |
| Coefficient of Thermal Expansion | 80x10⁻⁶ | K-1 | ASTM D 696 |
| Coefficient of Thermal Conductivity | 0.1 | W/(m.K) | ASTM C 177 |
| Specific Heat | 0.3 | kJ/(kg.K) | — |
| Value | Units | Test Method / Conditions | |
| Loctite® Equivalent | 290.0 | — | — |
| Permabond® Equivalent | HL126 | — | — |
| Value | Units | Test Method / Conditions | |
| Initial Strength Retained for Acetone (at 22ºC, 500hrs) | 95 | % | — |
| Initial Strength Retained for Ethanol (at 22ºC, 500hrs) | 95 | % | — |
| Initial Strength Retained for Motor Oil (at 125ºC, 500hrs) | 85 | % | — |
| Initial Strength Retained for Gasoline (at 22ºC, 500hrs) | 90 | % | — |
| Initial Strength Retained for Brake Fluid (at 22ºC, 500hrs) | 90 | % | — |
| Initial Strength Retained for Water/Glycol (at 87ºC, 500hrs) | 90 | % | — |
| Initial Strength Retained for Acetone (at 22ºC, 1000hrs) | 95 | % | — |
| Initial Strength Retained for Ethanol (at 22ºC, 1000hrs) | 95 | % | — |
| Initial Strength Retained for Motor Oil (at 125ºC, 1000hrs) | 50 | % | — |
| Initial Strength Retained for Gasoline (at 22ºC, 1000hrs) | 90 | % | — |
| Initial Strength Retained for Brake Fluid (at 22ºC, 1000hrs) | 85 | % | — |
| Initial Strength Retained for Water/Glycol (at 87ºC, 1000hrs) | 90 | % | — |
| Value | Units | Test Method / Conditions | |
| Handling Cure Time | 20 | minutes | — |
| Functional Cure Time | 1 - 3 | hrs | — |
| Full Cure Time | 24 | hrs | — |
| Breakaway Torque (M10 Steel Nuts and Bolts) | 10 (85) | N.m (lbs.in) | ISO 10964 |
| Prevail Torque (M10 Steel Nuts and Bolts) | 29 (250) | N.m (lbs.in) | ISO 10964 |
| Break Loose Torque (M10 Steel Nuts and Bolts, Pre-Torqued to 5 Nm) | 30 (270) | N.m (lbs.in) | ISO 10964 |
| Maximum Prevail Torque (M10 Steel Nuts and Bolts, Pre-Torqued to 5 Nm) | 40 (350) | N.m (lbs.in) | ISO 10964 |
| Compressive Shear Strength of Steel Pins and Collars | 5.4 (780) | N/mm² (psi) | ISO 10123 |
| Temperature Range | -55 to 150 | ºC | — |
| Value | Units | Test Method / Conditions | |
| Color | Green | — | — |
| Composition | Methacrylate ester | — | — |
| Viscosity (at 20 rpm, 25ºC, Brookfield RVT Spindle 3) | 12 | cPs | — |
| Specific Gravity | 1.07 | — | — |
Safety & Health
- Precautions
This product and the auxiliary materials normally combined with it are capable of producing adverse health effects ranging from minor skin irritation to serious systemic effects. None of these materials should be used, stored, or transported until the handling precautions and recommendations as stated in the Material Safety Data Sheets (MSDS).
Storage & Handling
- Shelf Life
- 2 Years
- Storage Information
Anaerobic adhesives are ideally stored in a cool, dry place in unopened containers at a room temperature between 46°F to 82°F. Please do not return unused material to its original container.