Features & Benefits
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
• Small and medium size containers for household and industrial chemicals.
- Processing conditions
Typical processing conditions: 160 – 200 ºC
Properties
- Mechanical Properties
- Thermal Properties
- Neat Resin Properties
Value | Units | Test Method / Conditions | |
Tensile Strength at Yield | 27 | MPa | ASTM D638 |
Tensile Strength at Break | 34 | MPa | ASTM D638 |
Tensile Elongation at Break | 740 | % | ASTM D638 |
Flexural Modulus | 1200 | MPa | ASTM D790 |
Tensile Impact | 200 | kJ/m2 | ASTM D1822 |
Izod Impact, Notched 23ºC | 10 | kJ/m2 | ASTM D256 |
Izod Impact, Notched -30ºC | 5 | kJ/m2 | ASTM D256 |
Hardness | 68 | Shore D | ASTM D2240 |
ESCR (Igepal10%) F50 | 63 | Hr. | ASTM D1693 |
Value | Units | Test Method / Conditions | |
Vicat Softening Temperature at 10N | 127 | ºC | ASTM D1525 |
Value | Units | Test Method / Conditions | |
MFR (190ºC/2.16Kg) | 0.3 | g/10min | ASTM D1238 |
MFR (190ºC/5.0Kg) | 1.4 | g/10min | ASTM D1240 |
Density | 0.954 | g/cm3 | ASTM D792 Method A |
Storage & Handling
- Storage and handling
B2555 should be stored in a dry cool place with adequate ventilation and protected from UV-light at temperatures below 50°C. It is advisable to process polyethylene resins within 6 months after delivery.