Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
• Food packaging
• Printing lamination
• Adhesive tape
• Stationary Packaging
• Metalized film- Processing conditions
- Recommended Extrusion Temperature: 190 – 250 ºC,
- Stretching Temperature: 130 – 160 ºC
- Stretching Ratio MD/TD: 4-7 / 7-10.
Properties
- Mechanical Properties
- Thermal Properties
- Film Properties
- Neat Resin Properties
Value | Units | Test Method / Conditions | |
Tensile Strength at Yield | 32 | MPa | ASTM D638 |
Tensile Elongation at Yield | 9 | % | ASTM D638 |
Tensile Strength at Break | 19 | MPa | ASTM D638 |
Tensile Elongation at Break | 155 | % | ASTM D638 |
Flexural Modulus | 1280 | MPa | ASTM D790 |
Flexural Strength | 34 | MPa | ASTM D790 |
Izod Impact, Notched 23ºC | 2.9 | kJ/m2 | ASTM D256 |
Rockwell Hardness | 98 | — | ASTM D785 |
Value | Units | Test Method / Conditions | |
Vicat Softening Temperature at 10N | 153 | ºC | ASTM D1525 |
Value | Units | Test Method / Conditions | |
Tensile Strength at Break (MD) | 110 | MPa | ASTM D882 |
Tensile Strength at Break (TD) | 215 | MPa | ASTM D882 |
Tensile Elongation at Break (MD) | 85 | % | ASTM D882 |
Tensile Elongation at Break (TD) | 17 | % | ASTM D883 |
1% Secant Modulus (MD) | 2050 | MPa | ASTM D884 |
1% Secant Modulus (TD) | 3700 | MPa | ASTM D885 |
Haze | 0.2 | % | ASTM D1003 |
Gloss 45º | 155 | -- | ASTM D2457 |
Value | Units | Test Method / Conditions | |
MFR (230ºC/2.16Kg) | 2.2 | g/10min | ASTM D1238 |
Density | 0.9 | g/cm3 | ASTM D792 Method A |
Storage & Handling
- Storage and handling
FS2011E should be stored in a dry cool place with adequate ventilation and protected from UV-light at temperature below 50 ºC. It is advisable to process polypropylene resins within 6 months after delivery.