Features & Benefits
- Materials Features
- Key Features
Good chemical, physical and electrical properties.
Applications & Uses
- Applications
- Plastics & Elastomers Processing Methods
- Applications
- Injection and extrusion molding
- Excellent mechanical performance
- High productivity
- Great surface appearance
- Good processing at high temperatures
Properties
- Color
- Flame Rating
- Mechanical Properties
- Physical Properties
- Typical Properties
- Thermal Properties
- Properties
- Fiberglass composites with up to 50% filler.
- Flame propagation resistance: GWT 960°C.
- Development of specific colors with Nylon base.
- Additives for UV protection applications.
| Value | Units | Test Method / Conditions | |
| Color | Natural | — | — |
| Drying (90°C) | 4 | Hours | — |
| Stress at Break (Cond.) | 180 | MPa | ISO 527 |
| Tensile Modulus (Cond.) | 13000 | MPa | ISO 527 |
| Tensile Modulus (Dry) | 17000 | MPa | ISO 527 |
| Value | Units | Test Method / Conditions | |
| Flexural Strength (Cond.) | 250 | MPa | ISO 178 |
| Flexural Strength (Dry) | 345 | MPa | ISO 178 |
| Izod Notched Impact Strength (23°C, Cond.) | 18 | kJ/m² | ISO 180/A |
| Izod Notched Impact Strength (23°C, Dry) | 14 | kJ/m² | ISO 180/A |
| Stress at Break (Dry) | 245 | MPa | ISO 527 |
| Value | Units | Test Method / Conditions | |
| Density | 1.57 | g/cm³ | ISO 1183 |
| Flame Rating (3.2mm) | HB | — | UL94 |
| Humidity Absorption (Cond.) | 1.2 | % | ISO 62 |
| Melting Point | 263 | °C | ISO 75-1-2 |
| Molding Process Temperature | 270 - 290 | °C | — |
| Mold Shrinkage (Dry, Flow, 3.18mm) | 0.8 | — | ISO 294-4 |
| Mold Shrinkage (Dry, Parallel, 3.18mm) | 0.3 | — | ISO 294-4 |
| Water absorption (Cond.) | 4.2 | % | ISO 62 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature (1.80MPa) | 244 | °C | — |
| Mold Temperature | 60 - 90 | °C | — |
| Strain at Break (Cond.) | 3.2 | % | ISO 527 |
| Strain at Break (Dry) | 2.3 | % | ISO 527 |