Properties
- Color
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Compression Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.57 | g/cm³ | ASTM D1895 |
Arc Resistance | 180 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.0e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 525 | V | ASTM D3638 |
Compressive Strength | 160 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 174 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 7.8 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.077 | — | ASTM D150 |
Flexural Modulus | 8892 | MPa | ASTM D790 |
Flexural Strength | 94.3 | MPa | ASTM D790 |
Heat Resistance | 150 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 119 | J/m | Plenco |
Impact Strength (Notched, Izod) | 19.4 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 19.9 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0077 | m/m | ASTM D6289 |
Oxygen Index | 32.6 | % | ASTM D2863 |
Permittivity (at 1MHz) | 7.1 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 1.05 | % | ASTM D6289 |
Rockwell Hardness | 73 | E-Scale | ASTM D785 |
Specific Gravity | 1.59 | — | ASTM D792 |
Tensile Elongation | 0.8 | % | ASTM D638 |
Tensile Modulus | 10237 | MPa | ASTM D638 |
Tensile Strength | 65 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.58 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-0 | — | UL 94 |
Volume Resistivity | 3300000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.35 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.58 | g/cm³ | ASTM D1895 |
Arc Resistance | 186 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.0e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 423 | V | ASTM D3638 |
Compressive Strength | 165 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 184 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 12 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.054 | — | ASTM D150 |
Flexural Modulus | 8856 | MPa | ASTM D790 |
Flexural Strength | 89.5 | MPa | ASTM D790 |
Heat Resistance | 152 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 148 | J/m | Plenco |
Impact Strength (Notched, Izod) | 20.1 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 22.1 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0042 | m/m | ASTM D6289 |
Oxygen Index | 32.6 | % | ASTM D2863 |
Permittivity (at 1MHz) | 6.5 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.89 | % | ASTM D6289 |
Rockwell Hardness | 71 | E-Scale | ASTM D785 |
Specific Gravity | 1.6 | — | ASTM D792 |
Tensile Elongation | 0.6 | % | ASTM D638 |
Tensile Modulus | 10039 | MPa | ASTM D638 |
Tensile Strength | 56 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.58 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-0 | — | UL 94 |
Volume Resistivity | 18000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.36 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.58 | g/cm³ | ASTM D1895 |
Arc Resistance | 186 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.0e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 498 | V | ASTM D3638 |
Compressive Strength | 166 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 186 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 7.7 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.073 | — | ASTM D150 |
Flexural Modulus | 8513 | MPa | ASTM D790 |
Flexural Strength | 84.6 | MPa | ASTM D790 |
Heat Resistance | 155 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 101 | J/m | Plenco |
Impact Strength (Notched, Izod) | 19.3 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 21.5 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0068 | m/m | ASTM D6289 |
Oxygen Index | 32.6 | % | ASTM D2863 |
Permittivity (at 1MHz) | 7.3 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.96 | % | ASTM D6289 |
Rockwell Hardness | 76 | E-Scale | ASTM D785 |
Specific Gravity | 1.6 | — | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 10763 | MPa | ASTM D638 |
Tensile Strength | 56 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.58 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-0 | — | UL 94 |
Volume Resistivity | 1500000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.43 | % | ASTM D570 |