Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Technologies
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Processing Information (Compression Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.68 | g/cm³ | ASTM D1895 |
Arc Resistance | 190 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.0e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 600 | V | ASTM D3638 |
Compressive Strength | 153 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 200 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 12.6 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.028 | — | ASTM D150 |
Flexural Modulus | 10754 | MPa | ASTM D790 |
Flexural Strength | 90.5 | MPa | ASTM D790 |
Heat Resistance | 167 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 137 | J/m | Plenco |
Impact Strength (Notched, Izod) | 24.8 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 26.5 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0031 | m/m | ASTM D6289 |
Oxygen Index | 24.2 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.3 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.04 | % | ASTM D6289 |
Rockwell Hardness | 70 | E-Scale | ASTM D785 |
Specific Gravity | 1.89 | — | ASTM D792 |
Tensile Elongation | 0.6 | % | ASTM D638 |
Tensile Modulus | 12024 | MPa | ASTM D638 |
Tensile Strength | 43 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.7 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 320000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.3 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.73 | g/cm³ | ASTM D1895 |
Arc Resistance | 189 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.0e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 600 | V | ASTM D3638 |
Compressive Strength | 162 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 211 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 12.4 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.028 | — | ASTM D150 |
Flexural Modulus | 11645 | MPa | ASTM D790 |
Flexural Strength | 92.5 | MPa | ASTM D790 |
Heat Resistance | 171 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 126 | J/m | Plenco |
Impact Strength (Notched, Izod) | 23 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 25.3 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0055 | m/m | ASTM D6289 |
Oxygen Index | 24.2 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.2 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.02 | % | ASTM D6289 |
Rockwell Hardness | 71 | E-Scale | ASTM D785 |
Specific Gravity | 1.89 | — | ASTM D792 |
Tensile Elongation | 0.6 | % | ASTM D638 |
Tensile Modulus | 11822 | MPa | ASTM D638 |
Tensile Strength | 51 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.7 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 240000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.3 | % | ASTM D570 |
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories