Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Technologies
Features & Benefits
- Labeling Claims
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.96 | g/cm³ | ASTM D1895 |
Arc Resistance | 191 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 4.6e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 600 | V | ASTM D3638 |
Compressive Strength | 156 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 249 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 15.4 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.016 | — | ASTM D150 |
Flexural Modulus | 19205 | MPa | ASTM D790 |
Flexural Strength | 113.9 | MPa | ASTM D790 |
Heat Resistance | 215 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 127 | J/m | Plenco |
Impact Strength (Notched, Izod) | 22.6 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 22.9 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0037 | m/m | ASTM D6289 |
Oxygen Index | 25 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.6 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0 | % | ASTM D6289 |
Rockwell Hardness | 72 | E-Scale | ASTM D785 |
Specific Gravity | 2.02 | — | ASTM D792 |
Tensile Elongation | 0.5 | % | ASTM D638 |
Tensile Modulus | 20622 | MPa | ASTM D638 |
Tensile Strength | 75 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.73 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 3600000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.13 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.91 | g/cm³ | ASTM D1895 |
Arc Resistance | 192 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 4.6e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 600 | V | ASTM D3638 |
Compressive Strength | 190 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 253 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 15.5 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.015 | — | ASTM D150 |
Flexural Modulus | 19562 | MPa | ASTM D790 |
Flexural Strength | 117.1 | MPa | ASTM D790 |
Heat Resistance | 213 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 119 | J/m | Plenco |
Impact Strength (Notched, Izod) | 22.5 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 27.5 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0019 | m/m | ASTM D6289 |
Oxygen Index | 25 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.7 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.01 | % | ASTM D6289 |
Rockwell Hardness | 79 | E-Scale | ASTM D785 |
Specific Gravity | 2.02 | — | ASTM D792 |
Tensile Elongation | 0.5 | % | ASTM D638 |
Tensile Modulus | 19968 | MPa | ASTM D638 |
Tensile Strength | 76 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.73 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 4200000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.13 | % | ASTM D570 |
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories