Properties
- Color
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.87 | g/cm³ | ASTM D1895 |
Arc Resistance | 190 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 4.6e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 600 | V | ASTM D3638 |
Compressive Strength | 166 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 262 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 15 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.016 | — | ASTM D150 |
Flexural Modulus | 17656 | MPa | ASTM D790 |
Flexural Strength | 135.3 | MPa | ASTM D790 |
Heat Resistance | 220 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 202 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 26.8 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 34 | J/m | ASTM D256 |
Mold Shrinkage * | 0.003 | m/m | ASTM D6289 |
Oxygen Index | 25.4 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.6 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.01 | % | ASTM D6289 |
Rockwell Hardness | 78 | E-Scale | ASTM D785 |
Specific Gravity | 1.99 | — | ASTM D792 |
Tensile Elongation | 0.6 | % | ASTM D638 |
Tensile Modulus | 20021 | MPa | ASTM D638 |
Tensile Strength | 83 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.72 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 2000000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.13 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.89 | g/cm³ | ASTM D1895 |
Arc Resistance | 191 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 4.6e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 600 | V | ASTM D3638 |
Compressive Strength | 205 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 265 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 14.8 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.015 | — | ASTM D150 |
Flexural Modulus | 18470 | MPa | ASTM D790 |
Flexural Strength | 140.4 | MPa | ASTM D790 |
Heat Resistance | 222 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 189 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 37.5 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 40.9 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0012 | m/m | ASTM D6289 |
Oxygen Index | 25.4 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.6 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.01 | % | ASTM D6289 |
Rockwell Hardness | 77 | E-Scale | ASTM D785 |
Specific Gravity | 1.99 | — | ASTM D792 |
Tensile Elongation | 0.6 | % | ASTM D638 |
Tensile Modulus | 18376 | MPa | ASTM D638 |
Tensile Strength | 85 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.72 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 2900000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.13 | % | ASTM D570 |