Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Technologies
Features & Benefits
- Labeling Claims
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Physical Form
- Processing Information (Injection Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.83 | g/cm³ | ASTM D1895 |
Arc Resistance | 189 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 6.7e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 600 | V | ASTM D3638 |
Compressive Strength | 130 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 267 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 14.4 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.021 | — | ASTM D150 |
Flexural Modulus | 10834 | MPa | ASTM D790 |
Flexural Strength | 106.6 | MPa | ASTM D790 |
Heat Resistance | 212 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 269 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 31.4 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 40.3 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0037 | m/m | ASTM D6289 |
Oxygen Index | 46.3 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.4 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.01 | % | ASTM D6289 |
Rockwell Hardness | 61 | E-Scale | ASTM D785 |
Specific Gravity | 1.83 | — | ASTM D792 |
Tensile Elongation | 1.1 | % | ASTM D638 |
Tensile Modulus | 11635 | MPa | ASTM D638 |
Tensile Strength | 66 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.91 | W/m/°C | ASTM E1461 |
UL Flammability (at 1mm) | V-0 | — | UL 94 |
Volume Resistivity | 1600000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.09 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.81 | g/cm³ | ASTM D1895 |
Arc Resistance | 189 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 6.7e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 600 | V | ASTM D3638 |
Compressive Strength | 178 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 277 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 14.4 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.018 | — | ASTM D150 |
Flexural Modulus | 10435 | MPa | ASTM D790 |
Flexural Strength | 119.5 | MPa | ASTM D790 |
Heat Resistance | 209 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 278 | J/m | Plenco |
Impact Strength (Notched, Izod) | 55.7 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 61 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0019 | m/m | ASTM D6289 |
Oxygen Index | 46.3 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.4 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.02 | % | ASTM D6289 |
Rockwell Hardness | 67 | E-Scale | ASTM D785 |
Specific Gravity | 1.83 | — | ASTM D792 |
Tensile Elongation | 0.9 | % | ASTM D638 |
Tensile Modulus | 12776 | MPa | ASTM D638 |
Tensile Strength | 76 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.91 | W/m/°C | ASTM E1461 |
UL Flammability (at 1mm) | V-0 | — | UL 94 |
Volume Resistivity | 1100000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.1 | % | ASTM D570 |