Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Technologies
Features & Benefits
- Labeling Claims
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.88 | g/cm³ | ASTM D1895 |
Arc Resistance | 189 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 6.8e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 600 | V | ASTM D3638 |
Compressive Strength | 119 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 253 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 13.1 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.017 | — | ASTM D150 |
Flexural Modulus | 10409 | MPa | ASTM D790 |
Flexural Strength | 102.6 | MPa | ASTM D790 |
Heat Resistance | 216 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 303 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 35.9 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 43.4 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0036 | m/m | ASTM D6289 |
Oxygen Index | 39.9 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.4 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.01 | % | ASTM D6289 |
Rockwell Hardness | 54 | E-Scale | ASTM D785 |
Specific Gravity | 1.89 | — | ASTM D792 |
Tensile Elongation | 1.1 | % | ASTM D638 |
Tensile Modulus | 11681 | MPa | ASTM D638 |
Tensile Strength | 65 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.87 | W/m/°C | ASTM E1461 |
UL Flammability (at 1mm) | V-0 | — | UL 94 |
Volume Resistivity | 1900000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.06 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.95 | g/cm³ | ASTM D1895 |
Arc Resistance | 187 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 6.8e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 600 | V | ASTM D3638 |
Compressive Strength | 157 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 267 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 12.4 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.013 | — | ASTM D150 |
Flexural Modulus | 10185 | MPa | ASTM D790 |
Flexural Strength | 119.1 | MPa | ASTM D790 |
Heat Resistance | 211 | °C | ASTM D794 |
Impact Strength (Notched, Charpy) | 72.4 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 77.4 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0019 | m/m | ASTM D6289 |
Oxygen Index | 39.9 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.2 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.01 | % | ASTM D6289 |
Rockwell Hardness | 51 | E-Scale | ASTM D785 |
Specific Gravity | 1.92 | — | ASTM D792 |
Tensile Elongation | 1.3 | % | ASTM D638 |
Tensile Modulus | 10819 | MPa | ASTM D638 |
Tensile Strength | 76 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.87 | W/m/°C | ASTM E1461 |
UL Flammability (at 1mm) | V-0 | — | UL 94 |
Volume Resistivity | 1200000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.07 | % | ASTM D570 |