Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
Features & Benefits
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Compression Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.59 | g/cm³ | ASTM D1895 |
Arc Resistance | 133 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.5e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 158 | V | ASTM D3638 |
Compressive Strength | 198 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 155 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 8.3 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.06 | — | ASTM D150 |
Flexural Modulus | 6862 | MPa | ASTM D790 |
Flexural Strength | 81.3 | MPa | ASTM D790 |
Heat Resistance | 198 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 94 | J/m | Plenco |
Impact Strength (Notched, Izod) | 15.6 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 17.9 | J/m | ASTM D256 |
Mold Shrinkage * | 0.01 | m/m | ASTM D6289 |
Oxygen Index | 28.4 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.4 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.39 | % | ASTM D6289 |
Rockwell Hardness | 86 | E-Scale | ASTM D785 |
Specific Gravity | 1.4 | — | ASTM D792 |
Tensile Elongation | 0.8 | % | ASTM D638 |
Tensile Modulus | 7590 | MPa | ASTM D638 |
Tensile Strength | 57 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.39 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-1 | — | UL 94 |
Volume Resistivity | 230000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.33 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.63 | g/cm³ | ASTM D1895 |
Arc Resistance | 132 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.5e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 167 | V | ASTM D3638 |
Compressive Strength | 212 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 176 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 12.2 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.052 | — | ASTM D150 |
Flexural Modulus | 8119 | MPa | ASTM D790 |
Flexural Strength | 92.3 | MPa | ASTM D790 |
Heat Resistance | 207 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 109 | J/m | Plenco |
Impact Strength (Notched, Izod) | 17.4 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 18.7 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0044 | m/m | ASTM D6289 |
Oxygen Index | 28.4 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.2 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.2 | % | ASTM D6289 |
Rockwell Hardness | 90 | E-Scale | ASTM D785 |
Specific Gravity | 1.39 | — | ASTM D792 |
Tensile Elongation | 0.6 | % | ASTM D638 |
Tensile Modulus | 8595 | MPa | ASTM D638 |
Tensile Strength | 51 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.39 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-1 | — | UL 94 |
Volume Resistivity | 320000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.4 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.6 | g/cm³ | ASTM D1895 |
Arc Resistance | 117 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.5e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 152 | V | ASTM D3638 |
Compressive Strength | 214 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 177 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 8.6 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.065 | — | ASTM D150 |
Flexural Modulus | 7101 | MPa | ASTM D790 |
Flexural Strength | 80.8 | MPa | ASTM D790 |
Heat Resistance | 197 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 98 | J/m | Plenco |
Impact Strength (Notched, Izod) | 18.1 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 19.5 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0065 | m/m | ASTM D6289 |
Oxygen Index | 28.4 | % | ASTM D2863 |
Permittivity (at 1MHz) | 6.1 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.21 | % | ASTM D6289 |
Rockwell Hardness | 91 | E-Scale | ASTM D785 |
Specific Gravity | 1.39 | — | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 7830 | MPa | ASTM D638 |
Tensile Strength | 54 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.39 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-1 | — | UL 94 |
Volume Resistivity | 270000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.32 | % | ASTM D570 |
Regulatory & Compliance
- Certifications & Compliance