Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
Features & Benefits
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Processing Information (Compression Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.6 | g/cm³ | ASTM D1895 |
Arc Resistance | 95 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 6.6e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 165 | V | ASTM D3638 |
Compressive Strength | 228 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 171 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 15.4 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.04 | — | ASTM D150 |
Flexural Modulus | 8698 | MPa | ASTM D790 |
Flexural Strength | 102.7 | MPa | ASTM D790 |
Heat Resistance | 201 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 116 | J/m | Plenco |
Impact Strength (Notched, Izod) | 18.6 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 19.1 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0043 | m/m | ASTM D6289 |
Oxygen Index | 25.8 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.8 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.19 | % | ASTM D6289 |
Rockwell Hardness | 94 | E-Scale | ASTM D785 |
Specific Gravity | 1.39 | — | ASTM D792 |
Tensile Elongation | 0.8 | % | ASTM D638 |
Tensile Modulus | 9236 | MPa | ASTM D638 |
Tensile Strength | 64 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.35 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 1800000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.37 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.59 | g/cm³ | ASTM D1895 |
Arc Resistance | 126 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 6.6e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 158 | V | ASTM D3638 |
Compressive Strength | 212 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 162 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 11.7 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.059 | — | ASTM D150 |
Flexural Modulus | 7597 | MPa | ASTM D790 |
Flexural Strength | 86.9 | MPa | ASTM D790 |
Heat Resistance | 198 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 109 | J/m | Plenco |
Impact Strength (Notched, Izod) | 17.9 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 19 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0072 | m/m | ASTM D6289 |
Oxygen Index | 25.8 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.26 | % | ASTM D6289 |
Rockwell Hardness | 88 | E-Scale | ASTM D785 |
Specific Gravity | 1.37 | — | ASTM D792 |
Tensile Elongation | 0.8 | % | ASTM D638 |
Tensile Modulus | 7905 | MPa | ASTM D638 |
Tensile Strength | 53 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.35 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 570000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.34 | % | ASTM D570 |
Regulatory & Compliance
- Certifications & Compliance