Value | Units | Test Method / Conditions | |
Apparent Density | 0.62 | g/cm³ | ASTM D1895 |
Arc Resistance | 141 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 6.5e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 175 | V | ASTM D3638 |
Compressive Strength | 189 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 141 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 11.3 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.053 | — | ASTM D150 |
Flexural Modulus | 7507 | MPa | ASTM D790 |
Flexural Strength | 87.4 | MPa | ASTM D790 |
Heat Resistance | 199 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 89 | J/m | Plenco |
Impact Strength (Notched, Izod) | 15.8 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 18.1 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0109 | m/m | ASTM D6289 |
Oxygen Index | 25.7 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.9 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.33 | % | ASTM D6289 |
Rockwell Hardness | 82 | E-Scale | ASTM D785 |
Specific Gravity | 1.41 | — | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 8457 | MPa | ASTM D638 |
Tensile Strength | 57 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.41 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 440000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.32 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.61 | g/cm³ | ASTM D1895 |
Arc Resistance | 124 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 6.5e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 175 | V | ASTM D3638 |
Compressive Strength | 214 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 176 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 14.4 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.042 | — | ASTM D150 |
Flexural Modulus | 8301 | MPa | ASTM D790 |
Flexural Strength | 91.7 | MPa | ASTM D790 |
Heat Resistance | 202 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 115 | J/m | Plenco |
Impact Strength (Notched, Izod) | 19.2 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 19.3 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0046 | m/m | ASTM D6289 |
Oxygen Index | 25.7 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.9 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.23 | % | ASTM D6289 |
Rockwell Hardness | 89 | E-Scale | ASTM D785 |
Specific Gravity | 1.42 | — | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 8796 | MPa | ASTM D638 |
Tensile Strength | 55 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.41 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 870000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.37 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.63 | g/cm³ | ASTM D1895 |
Arc Resistance | 141 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 6.5e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 175 | V | ASTM D3638 |
Compressive Strength | 208 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 172 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 11.7 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.054 | — | ASTM D150 |
Flexural Modulus | 8165 | MPa | ASTM D790 |
Flexural Strength | 87.5 | MPa | ASTM D790 |
Heat Resistance | 204 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 98 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 18.1 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 19.8 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0063 | m/m | ASTM D6289 |
Oxygen Index | 25.7 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.4 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.29 | % | ASTM D6289 |
Rockwell Hardness | 86 | E-Scale | ASTM D785 |
Specific Gravity | 1.43 | — | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 8072 | MPa | ASTM D638 |
Tensile Strength | 53 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.41 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 390000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.31 | % | ASTM D570 |