Properties
- Color
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Compression Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.61 | g/cm³ | ASTM D1895 |
Arc Resistance | 132 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 6.1e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 173 | V | ASTM D3638 |
Compressive Strength | 181 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 165 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 9.8 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.057 | — | ASTM D150 |
Flexural Modulus | 6770 | MPa | ASTM D790 |
Flexural Strength | 88.5 | MPa | ASTM D790 |
Heat Resistance | 187 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 111 | J/m | Plenco |
Impact Strength (Notched, Izod) | 17.2 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 17.9 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0085 | m/m | ASTM D6289 |
Oxygen Index | 25.5 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.7 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.56 | % | ASTM D6289 |
Rockwell Hardness | 70 | E-Scale | ASTM D785 |
Specific Gravity | 1.36 | — | ASTM D792 |
Tensile Elongation | 1.1 | % | ASTM D638 |
Tensile Modulus | 7377 | MPa | ASTM D638 |
Tensile Strength | 63 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.37 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 11000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.59 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.71 | g/cm³ | ASTM D1895 |
Arc Resistance | 130 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 6.1e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 175 | V | ASTM D3638 |
Compressive Strength | 165 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 194 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 13.7 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.046 | — | ASTM D150 |
Flexural Modulus | 8063 | MPa | ASTM D790 |
Flexural Strength | 78.2 | MPa | ASTM D790 |
Heat Resistance | 191 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 119 | J/m | Plenco |
Impact Strength (Notched, Izod) | 18.2 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 19.7 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0032 | m/m | ASTM D6289 |
Oxygen Index | 25.5 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.6 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.36 | % | ASTM D6289 |
Rockwell Hardness | 68 | E-Scale | ASTM D785 |
Specific Gravity | 1.43 | — | ASTM D792 |
Tensile Elongation | 0.8 | % | ASTM D638 |
Tensile Modulus | 8764 | MPa | ASTM D638 |
Tensile Strength | 56 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.37 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 24000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.54 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.61 | g/cm³ | ASTM D1895 |
Arc Resistance | 132 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 6.1e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 171 | V | ASTM D3638 |
Compressive Strength | 189 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 176 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 9.4 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.057 | — | ASTM D150 |
Flexural Modulus | 6831 | MPa | ASTM D790 |
Flexural Strength | 87.4 | MPa | ASTM D790 |
Heat Resistance | 185 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 105 | J/m | Plenco |
Impact Strength (Notched, Izod) | 17.8 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 18.9 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0069 | m/m | ASTM D6289 |
Oxygen Index | 25.5 | % | ASTM D2863 |
Permittivity (at 1MHz) | 6.1 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.49 | % | ASTM D6289 |
Rockwell Hardness | 73 | E-Scale | ASTM D785 |
Specific Gravity | 1.37 | — | ASTM D792 |
Tensile Elongation | 1 | % | ASTM D638 |
Tensile Modulus | 7110 | MPa | ASTM D638 |
Tensile Strength | 57 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.37 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 8300000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.63 | % | ASTM D570 |
Regulatory & Compliance
- Certifications & Compliance