Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
Features & Benefits
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Compression Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.64 | g/cm³ | ASTM D1895 |
Arc Resistance | 132 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.9e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 180 | V | ASTM D3638 |
Compressive Strength | 193 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 161 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 12.7 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.058 | — | ASTM D150 |
Flexural Modulus | 7762 | MPa | ASTM D790 |
Flexural Strength | 90.5 | MPa | ASTM D790 |
Heat Resistance | 200 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 110 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 18.9 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 19.3 | J/m | ASTM D256 |
Mold Shrinkage * | 0.009 | m/m | ASTM D6289 |
Oxygen Index | 27 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.6 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.29 | % | ASTM D6289 |
Rockwell Hardness | 86 | E-Scale | ASTM D785 |
Specific Gravity | 1.41 | — | ASTM D792 |
Tensile Elongation | 0.9 | % | ASTM D638 |
Tensile Modulus | 8869 | MPa | ASTM D638 |
Tensile Strength | 61 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.39 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 2500000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.3 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.62 | g/cm³ | ASTM D1895 |
Arc Resistance | 134 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.9e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 169 | V | ASTM D3638 |
Compressive Strength | 212 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 175 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 14.3 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.047 | — | ASTM D150 |
Flexural Modulus | 8471 | MPa | ASTM D790 |
Flexural Strength | 90.4 | MPa | ASTM D790 |
Heat Resistance | 205 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 109 | J/m | Plenco |
Impact Strength (Notched, Izod) | 16.9 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 19.1 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0048 | m/m | ASTM D6289 |
Oxygen Index | 27 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.2 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.17 | % | ASTM D6289 |
Rockwell Hardness | 87 | E-Scale | ASTM D785 |
Specific Gravity | 1.4 | — | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 8285 | MPa | ASTM D638 |
Tensile Strength | 53 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.39 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 800000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.4 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.6 | g/cm³ | ASTM D1895 |
Arc Resistance | 135 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.9e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 154 | V | ASTM D3638 |
Compressive Strength | 208 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 174 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 12.6 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.049 | — | ASTM D150 |
Flexural Modulus | 7499 | MPa | ASTM D790 |
Flexural Strength | 79.2 | MPa | ASTM D790 |
Heat Resistance | 197 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 103 | J/m | Plenco |
Impact Strength (Notched, Izod) | 17.1 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 19.5 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0076 | m/m | ASTM D6289 |
Oxygen Index | 27 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.8 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.25 | % | ASTM D6289 |
Rockwell Hardness | 88 | E-Scale | ASTM D785 |
Specific Gravity | 1.41 | — | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 8012 | MPa | ASTM D638 |
Tensile Strength | 52 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.39 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 690000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.32 | % | ASTM D570 |
Regulatory & Compliance
- Certifications & Compliance