Plastics Engineering Company 03356 Two-Stage Phenolic

Identification & Functionality

Chemical Family

Phenol Formaldehyde (PF),

Phenols & Phenolics

Polymer Name

Phenol Formaldehyde (PF)

Reinforcement Material

Mineral

Composite Materials Functions

Molding Compound

Technologies

Composite Materials

Product Families

Composite Materials — Prepregs & Molding Compounds

Other Prepregs & Molding Compounds

Features & Benefits

Materials Features

Arc Resistant,

Cost Effective,

Dimensional Stability,

Excellent Surface Hardness,

Excellent Track Resistance Properties,

Flame Resistant,

Good Compressive Strength,

Good Mechanical Properties,

Good Tracking Resistance,

Heat Resistance,

High Modulus,

Low Shrinkage,

Two-Stage,

UL Listed

Applications & Uses

Markets

Consumer Goods,

Electrical & Electronics

Applications

Consumer Goods — Appliances & Electronics

Electrical & Electronics — Devices & Assemblies

Automotive Electronics,

Consumer Electronics

Electrical & Electronics — Parts & Components

Housings & Enclosures,

Switches & Relays,

Terminal Blocks, Plugs & Sockets

Composites End Use

Cases,

Home Appliances,

Housings

Composites Processing Methods

Compression Molding,

Injection Molding

Plastics & Elastomers Processing Methods

Transfer Molding

Properties

Color

Black

Flame Rating

UL 94 V0

Physical Form

Granules,

Solid

Processing Information (Injection Molding)

	Value	Units	Test Method / Conditions
Apparent Density	0.66	g/cm³	ASTM D1895
Arc Resistance	180	sec	ASTM D495
Coefficient of Thermal Expansion	5.3e-05	per °C	ASTM E831
Comparative Tracking Index	184	V	ASTM D3638
Compressive Strength	159	MPa	ASTM D695
Deflection Temperature (at 1.82MPa)	166	°C	ASTM D648
Dielectric Strength (Short Time)	11	kV/mm	ASTM D149
Dissipation Factor (at 1MHz)	0.066	—	ASTM D150
Flexural Modulus	9004	MPa	ASTM D790
Flexural Strength	79.6	MPa	ASTM D790
Heat Resistance	204	°C	ASTM D794
Impact Strength (Drop Ball)	88	J/m	Plenco
Impact Strength (Notched, Charpy)	17	J/m	ASTM D256
Impact Strength (Notched, Izod)	17.2	J/m	ASTM D256
Mold Shrinkage *	0.0081	m/m	ASTM D6289
Oxygen Index	28.8	%	ASTM D2863
Permittivity (at 1MHz)	5.2	—	ASTM D150
Post Shrinkage (at 120°C, 72hr)	0.25	%	ASTM D6289
Rockwell Hardness	76	E-Scale	ASTM D785
Specific Gravity	1.56	—	ASTM D792
Tensile Elongation	0.6	%	ASTM D638
Tensile Modulus	10818	MPa	ASTM D638
Tensile Strength	51	MPa	ASTM D638
Thermal Conductivity (at 100°C)	0.58	W/m/°C	ASTM E1461
UL Flammability (at 1.5mm)	V-0	—	UL 94
Volume Resistivity	830000000000	ohm·cm	ASTM D257
Water Absorption	0.22	%	ASTM D570

Processing Information (Compression Molding)

	Value	Units	Test Method / Conditions
Apparent Density	0.68	g/cm³	ASTM D1895
Arc Resistance	184	sec	ASTM D495
Coefficient of Thermal Expansion	5.3e-05	per °C	ASTM E831
Comparative Tracking Index	183	V	ASTM D3638
Compressive Strength	164	MPa	ASTM D695
Deflection Temperature (at 1.82MPa)	195	°C	ASTM D648
Dielectric Strength (Short Time)	16.3	kV/mm	ASTM D149
Dissipation Factor (at 1MHz)	0.036	—	ASTM D150
Flexural Modulus	9986	MPa	ASTM D790
Flexural Strength	72	MPa	ASTM D790
Heat Resistance	211	°C	ASTM D794
Impact Strength (Drop Ball)	115	J/m	Plenco
Impact Strength (Notched, Izod)	18.4	J/m	ASTM D256
Impact Strength (Notched, Charpy)	20.6	J/m	ASTM D256
Mold Shrinkage *	0.0023	m/m	ASTM D6289
Oxygen Index	28.8	%	ASTM D2863
Permittivity (at 1MHz)	4.4	—	ASTM D150
Post Shrinkage (at 120°C, 72hr)	0.08	%	ASTM D6289
Rockwell Hardness	79	E-Scale	ASTM D785
Specific Gravity	1.56	—	ASTM D792
Tensile Elongation	0.5	%	ASTM D638
Tensile Modulus	11148	MPa	ASTM D638
Tensile Strength	50	MPa	ASTM D638
Thermal Conductivity (at 100°C)	0.58	W/m/°C	ASTM E1461
UL Flammability (at 1.5mm)	V-0	—	UL 94
Volume Resistivity	20000000000000	ohm·cm	ASTM D257
Water Absorption	0.22	%	ASTM D570

Processing Information (Transfer Molding)

	Value	Units	Test Method / Conditions
Apparent Density	0.66	g/cm³	ASTM D1895
Arc Resistance	180	sec	ASTM D495
Coefficient of Thermal Expansion	5.3e-05	per °C	ASTM E831
Comparative Tracking Index	182	V	ASTM D3638
Compressive Strength	161	MPa	ASTM D695
Deflection Temperature (at 1.82MPa)	191	°C	ASTM D648
Dielectric Strength (Short Time)	11.4	kV/mm	ASTM D149
Dissipation Factor (at 1MHz)	0.065	—	ASTM D150
Flexural Modulus	10344	MPa	ASTM D790
Flexural Strength	87.8	MPa	ASTM D790
Heat Resistance	208	°C	ASTM D794
Impact Strength (Drop Ball)	86	J/m	Plenco
Impact Strength (Notched, Izod)	20	J/m	ASTM D256
Impact Strength (Notched, Charpy)	20.9	J/m	ASTM D256
Mold Shrinkage *	0.0042	m/m	ASTM D6289
Oxygen Index	28.8	%	ASTM D2863
Permittivity (at 1MHz)	5.6	—	ASTM D150
Post Shrinkage (at 120°C, 72hr)	0.16	%	ASTM D6289
Rockwell Hardness	79	E-Scale	ASTM D785
Specific Gravity	1.57	—	ASTM D792
Tensile Elongation	0.5	%	ASTM D638
Tensile Modulus	10585	MPa	ASTM D638
Tensile Strength	47	MPa	ASTM D638
Thermal Conductivity (at 100°C)	0.58	W/m/°C	ASTM E1461
UL Flammability (at 1.5mm)	V-0	—	UL 94
Volume Resistivity	510000000000	ohm·cm	ASTM D257
Water Absorption	0.17	%	ASTM D570

Regulatory & Compliance

Certifications & Compliance

UL 94