Features & Benefits
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Compression Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.66 | g/cm³ | ASTM D1895 |
Arc Resistance | 180 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 4.9e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 179 | V | ASTM D3638 |
Compressive Strength | 162 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 173 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 11.1 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.058 | — | ASTM D150 |
Flexural Modulus | 8754 | MPa | ASTM D790 |
Flexural Strength | 85.3 | MPa | ASTM D790 |
Heat Resistance | 202 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 100 | J/m | Plenco |
Impact Strength (Notched, Izod) | 17.1 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 17.9 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0076 | m/m | ASTM D6289 |
Oxygen Index | 32.3 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.5 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.25 | % | ASTM D6289 |
Rockwell Hardness | 77 | E-Scale | ASTM D785 |
Specific Gravity | 1.54 | — | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 9902 | MPa | ASTM D638 |
Tensile Strength | 53 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.54 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-0 | — | UL 94 |
Volume Resistivity | 910000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.22 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.72 | g/cm³ | ASTM D1895 |
Arc Resistance | 180 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 4.9e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 188 | V | ASTM D3638 |
Compressive Strength | 194 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 192 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 14.6 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.039 | — | ASTM D150 |
Flexural Modulus | 10497 | MPa | ASTM D790 |
Flexural Strength | 79.6 | MPa | ASTM D790 |
Heat Resistance | 205 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 96 | J/m | Plenco |
Impact Strength (Notched, Izod) | 16.6 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 20.3 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0031 | m/m | ASTM D6289 |
Oxygen Index | 32.3 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.1 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.13 | % | ASTM D6289 |
Rockwell Hardness | 84 | E-Scale | ASTM D785 |
Specific Gravity | 1.57 | — | ASTM D792 |
Tensile Elongation | 0.5 | % | ASTM D638 |
Tensile Modulus | 11253 | MPa | ASTM D638 |
Tensile Strength | 46 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.54 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-0 | — | UL 94 |
Volume Resistivity | 1900000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.19 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.65 | g/cm³ | ASTM D1895 |
Arc Resistance | 182 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 4.9e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 176 | V | ASTM D3638 |
Compressive Strength | 172 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 194 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 12 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.058 | — | ASTM D150 |
Flexural Modulus | 9417 | MPa | ASTM D790 |
Flexural Strength | 91.6 | MPa | ASTM D790 |
Heat Resistance | 203 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 92 | J/m | Plenco |
Impact Strength (Notched, Izod) | 20.2 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 21.5 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0042 | m/m | ASTM D6289 |
Oxygen Index | 32.3 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.7 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.16 | % | ASTM D6289 |
Rockwell Hardness | 79 | E-Scale | ASTM D785 |
Specific Gravity | 1.55 | — | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 9984 | MPa | ASTM D638 |
Tensile Strength | 55 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.54 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-0 | — | UL 94 |
Volume Resistivity | 400000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.16 | % | ASTM D570 |