Plastics Engineering Company 04349 Two-Stage Phenolic

Identification & Functionality

Chemical Family

Phenol Formaldehyde (PF),

Phenols & Phenolics

Polymer Name

Phenol Formaldehyde (PF)

Reinforcement Material

Mineral

Composite Materials Functions

Molding Compound

Technologies

Composite Materials

Product Families

Composite Materials — Prepregs & Molding Compounds

Other Prepregs & Molding Compounds

Features & Benefits

Materials Features

Arc Resistant,

Cost Effective,

Dimensional Stability,

Excellent Track Resistance Properties,

Good Mechanical Properties,

Heat Resistance,

High Temperature Strength,

Two-Stage,

UL Listed

Applications & Uses

Markets

Consumer Goods,

Electrical & Electronics

Applications

Consumer Goods — Appliances & Electronics

Electrical & Electronics — Devices & Assemblies

Consumer Electronics

Consumer Goods — Housewares

Electrical & Electronics — Parts & Components

Connectors,

Housings & Enclosures,

Terminal Blocks, Plugs & Sockets

Composites End Use

Cases,

Home Appliances,

Housings

Composites Processing Methods

Compression Molding,

Injection Molding

Plastics & Elastomers Processing Methods

Transfer Molding

Properties

Color

Black

Flame Rating

UL 94 V1

Physical Form

Granules,

Solid

Processing Information (Injection Molding)

	Value	Units	Test Method / Conditions
Apparent Density	0.63	g/cm³	ASTM D1895
Arc Resistance	163	sec	ASTM D495
Coefficient of Thermal Expansion	3.9e-05	per °C	ASTM E831
Comparative Tracking Index	176	V	ASTM D3638
Compressive Strength	186	MPa	ASTM D695
Deflection Temperature (at 1.82MPa)	161	°C	ASTM D648
Dielectric Strength (Short Time)	10.1	kV/mm	ASTM D149
Dissipation Factor (at 1MHz)	0.059	—	ASTM D150
Flexural Modulus	8741	MPa	ASTM D790
Flexural Strength	78.8	MPa	ASTM D790
Heat Resistance	215	°C	ASTM D794
Impact Strength (Drop Ball)	76	J/m	Plenco
Impact Strength (Notched, Izod)	14.9	J/m	ASTM D256
Impact Strength (Notched, Charpy)	16	J/m	ASTM D256
Mold Shrinkage *	0.0067	m/m	ASTM D6289
Oxygen Index	37.9	%	ASTM D2863
Permittivity (at 1MHz)	5.8	—	ASTM D150
Post Shrinkage (at 120°C, 72hr)	0.17	%	ASTM D6289
Rockwell Hardness	84	E-Scale	ASTM D785
Specific Gravity	1.56	—	ASTM D792
Tensile Elongation	0.7	%	ASTM D638
Tensile Modulus	9557	MPa	ASTM D638
Tensile Strength	50	MPa	ASTM D638
Thermal Conductivity (at 100°C)	0.49	W/m/°C	ASTM E1461
UL Flammability (at 1.5mm)	V-1	—	UL 94
Volume Resistivity	640000000000	ohm·cm	ASTM D257
Water Absorption	0.1	%	ASTM D570

Processing Information (Compression Molding)

	Value	Units	Test Method / Conditions
Apparent Density	0.65	g/cm³	ASTM D1895
Arc Resistance	176	sec	ASTM D495
Coefficient of Thermal Expansion	3.9e-05	per °C	ASTM E831
Comparative Tracking Index	178	V	ASTM D3638
Compressive Strength	199	MPa	ASTM D695
Deflection Temperature (at 1.82MPa)	209	°C	ASTM D648
Dielectric Strength (Short Time)	11.2	kV/mm	ASTM D149
Dissipation Factor (at 1MHz)	0.056	—	ASTM D150
Flexural Modulus	9363	MPa	ASTM D790
Flexural Strength	70.3	MPa	ASTM D790
Heat Resistance	232	°C	ASTM D794
Impact Strength (Drop Ball)	78	J/m	Plenco
Impact Strength (Notched, Izod)	14.6	J/m	ASTM D256
Impact Strength (Notched, Charpy)	19.1	J/m	ASTM D256
Mold Shrinkage *	0.0026	m/m	ASTM D6289
Oxygen Index	37.9	%	ASTM D2863
Permittivity (at 1MHz)	6.1	—	ASTM D150
Post Shrinkage (at 120°C, 72hr)	0.15	%	ASTM D6289
Rockwell Hardness	89	E-Scale	ASTM D785
Specific Gravity	1.57	—	ASTM D792
Tensile Elongation	0.5	%	ASTM D638
Tensile Modulus	10083	MPa	ASTM D638
Tensile Strength	46	MPa	ASTM D638
Thermal Conductivity (at 100°C)	0.49	W/m/°C	ASTM E1461
UL Flammability (at 1.5mm)	V-1	—	UL 94
Volume Resistivity	690000000000	ohm·cm	ASTM D257
Water Absorption	0.11	%	ASTM D570

Processing Information (Transfer Molding)

	Value	Units	Test Method / Conditions
Apparent Density	0.66	g/cm³	ASTM D1895
Arc Resistance	174	sec	ASTM D495
Coefficient of Thermal Expansion	3.9e-05	per °C	ASTM E831
Comparative Tracking Index	179	V	ASTM D3638
Compressive Strength	203	MPa	ASTM D695
Deflection Temperature (at 1.82MPa)	213	°C	ASTM D648
Dielectric Strength (Short Time)	11.7	kV/mm	ASTM D149
Dissipation Factor (at 1MHz)	0.071	—	ASTM D150
Flexural Modulus	8862	MPa	ASTM D790
Flexural Strength	77.4	MPa	ASTM D790
Heat Resistance	217	°C	ASTM D794
Impact Strength (Drop Ball)	94	J/m	Plenco
Impact Strength (Notched, Izod)	15.7	J/m	ASTM D256
Impact Strength (Notched, Charpy)	18.9	J/m	ASTM D256
Mold Shrinkage *	0.0041	m/m	ASTM D6289
Oxygen Index	37.9	%	ASTM D2863
Permittivity (at 1MHz)	5.9	—	ASTM D150
Post Shrinkage (at 120°C, 72hr)	0.17	%	ASTM D6289
Rockwell Hardness	92	E-Scale	ASTM D785
Specific Gravity	1.57	—	ASTM D792
Tensile Elongation	0.7	%	ASTM D638
Tensile Modulus	9560	MPa	ASTM D638
Tensile Strength	54	MPa	ASTM D638
Thermal Conductivity (at 100°C)	0.49	W/m/°C	ASTM E1461
UL Flammability (at 1.5mm)	V-1	—	UL 94
Volume Resistivity	340000000000	ohm·cm	ASTM D257
Water Absorption	0.13	%	ASTM D570

Regulatory & Compliance

Certifications & Compliance

UL 94