Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Technologies
Features & Benefits
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.62 | g/cm³ | ASTM D1895 |
Arc Resistance | 145 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.7e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 188 | V | ASTM D3638 |
Compressive Strength | 177 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 168 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 12.8 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.049 | — | ASTM D150 |
Flexural Modulus | 8140 | MPa | ASTM D790 |
Flexural Strength | 86.1 | MPa | ASTM D790 |
Heat Resistance | 200 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 113 | J/m | Plenco |
Impact Strength (Notched, Izod) | 17.9 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 20 | J/m | ASTM D256 |
Mold Shrinkage * | 0.007 | m/m | ASTM D6289 |
Oxygen Index | 30.8 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.2 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.23 | % | ASTM D6289 |
Rockwell Hardness | 65 | E-Scale | ASTM D785 |
Specific Gravity | 1.54 | — | ASTM D792 |
Tensile Elongation | 0.8 | % | ASTM D638 |
Tensile Modulus | 9746 | MPa | ASTM D638 |
Tensile Strength | 54 | MPa | ASTM D638 |
UL Flammability (at 1.5mm) | V-1 | — | UL 94 |
Volume Resistivity | 630000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.27 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.63 | g/cm³ | ASTM D1895 |
Arc Resistance | 162 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.7e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 183 | V | ASTM D3638 |
Compressive Strength | 175 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 195 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 11.9 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.051 | — | ASTM D150 |
Flexural Modulus | 9526 | MPa | ASTM D790 |
Flexural Strength | 94 | MPa | ASTM D790 |
Heat Resistance | 203 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 113 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 21.8 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 23.6 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0034 | m/m | ASTM D6289 |
Oxygen Index | 30.8 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.3 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.15 | % | ASTM D6289 |
Rockwell Hardness | 79 | E-Scale | ASTM D785 |
Specific Gravity | 1.54 | — | ASTM D792 |
Tensile Elongation | 0.6 | % | ASTM D638 |
Tensile Modulus | 10142 | MPa | ASTM D638 |
Tensile Strength | 52 | MPa | ASTM D638 |
UL Flammability (at 1.5mm) | V-1 | — | UL 94 |
Volume Resistivity | 410000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.21 | % | ASTM D570 |
Regulatory & Compliance
- Certifications & Compliance