Plastics Engineering Company 04466 Two-Stage Phenolic

Identification & Functionality

Chemical Family

Phenol Formaldehyde (PF),

Phenols & Phenolics

Polymer Name

Phenol Formaldehyde (PF)

Reinforcement Material

Mineral

Composite Materials Functions

Molding Compound

Technologies

Composite Materials

Product Families

Composite Materials — Prepregs & Molding Compounds

Other Prepregs & Molding Compounds

Features & Benefits

Materials Features

Arc Resistant,

Cost Effective,

Dimensional Stability,

Excellent Mechanical Strength,

Excellent Track Resistance Properties,

Good Mechanical Properties,

Heat Resistance,

High Temperature Strength,

Two-Stage,

UL Listed

Applications & Uses

Markets

Consumer Goods,

Electrical & Electronics

Applications

Consumer Goods — Appliances & Electronics

Electrical & Electronics — Devices & Assemblies

Consumer Electronics

Consumer Goods — Housewares

Electrical & Electronics — Parts & Components

Connectors,

Housings & Enclosures,

Terminal Blocks, Plugs & Sockets

Composites End Use

Cases,

Home Appliances,

Housings

Composites Processing Methods

Compression Molding,

Injection Molding

Plastics & Elastomers Processing Methods

Transfer Molding

Properties

Color

Black

Flame Rating

UL 94 V0

Physical Form

Granules,

Solid

Processing Information (Injection Molding)

	Value	Units	Test Method / Conditions
Apparent Density	0.63	g/cm³	ASTM D1895
Arc Resistance	181	sec	ASTM D495
Coefficient of Thermal Expansion	4.3e-05	per °C	ASTM E831
Comparative Tracking Index	182	V	ASTM D3638
Compressive Strength	155	MPa	ASTM D695
Deflection Temperature (at 1.82MPa)	162	°C	ASTM D648
Dielectric Strength (Short Time)	10.6	kV/mm	ASTM D149
Dissipation Factor (at 1MHz)	0.069	—	ASTM D150
Flexural Modulus	8949	MPa	ASTM D790
Flexural Strength	83.8	MPa	ASTM D790
Heat Resistance	203	°C	ASTM D794
Impact Strength (Drop Ball)	100	J/m	Plenco
Impact Strength (Notched, Izod)	16.9	J/m	ASTM D256
Impact Strength (Notched, Charpy)	18.2	J/m	ASTM D256
Mold Shrinkage *	0.0076	m/m	ASTM D6289
Oxygen Index	28.1	%	ASTM D2863
Permittivity (at 1MHz)	5.8	—	ASTM D150
Post Shrinkage (at 120°C, 72hr)	0.27	%	ASTM D6289
Rockwell Hardness	73	E-Scale	ASTM D785
Specific Gravity	1.58	—	ASTM D792
Tensile Elongation	0.6	%	ASTM D638
Tensile Modulus	10519	MPa	ASTM D638
Tensile Strength	50	MPa	ASTM D638
Thermal Conductivity (at 100°C)	0.56	W/m/°C	ASTM E1461
UL Flammability (at 1.5mm)	V-0	—	UL 94
Volume Resistivity	200000000000	ohm·cm	ASTM D257
Water Absorption	0.18	%	ASTM D570

Processing Information (Compression Molding)

	Value	Units	Test Method / Conditions
Apparent Density	0.63	g/cm³	ASTM D1895
Arc Resistance	185	sec	ASTM D495
Coefficient of Thermal Expansion	4.3e-05	per °C	ASTM E831
Comparative Tracking Index	179	V	ASTM D3638
Compressive Strength	153	MPa	ASTM D695
Deflection Temperature (at 1.82MPa)	217	°C	ASTM D648
Dielectric Strength (Short Time)	13.9	kV/mm	ASTM D149
Dissipation Factor (at 1MHz)	0.048	—	ASTM D150
Flexural Modulus	9770	MPa	ASTM D790
Flexural Strength	63.2	MPa	ASTM D790
Heat Resistance	208	°C	ASTM D794
Impact Strength (Drop Ball)	118	J/m	Plenco
Impact Strength (Notched, Izod)	18	J/m	ASTM D256
Impact Strength (Notched, Charpy)	21.8	J/m	ASTM D256
Mold Shrinkage *	0.0031	m/m	ASTM D6289
Oxygen Index	28.1	%	ASTM D2863
Permittivity (at 1MHz)	5.5	—	ASTM D150
Post Shrinkage (at 120°C, 72hr)	0.15	%	ASTM D6289
Rockwell Hardness	79	E-Scale	ASTM D785
Specific Gravity	1.6	—	ASTM D792
Tensile Elongation	0.4	%	ASTM D638
Tensile Modulus	10920	MPa	ASTM D638
Tensile Strength	45	MPa	ASTM D638
Thermal Conductivity (at 100°C)	0.56	W/m/°C	ASTM E1461
UL Flammability (at 1.5mm)	V-0	—	UL 94
Volume Resistivity	2100000000000	ohm·cm	ASTM D257
Water Absorption	0.13	%	ASTM D570

Processing Information (Transfer Molding)

	Value	Units	Test Method / Conditions
Apparent Density	0.6	g/cm³	ASTM D1895
Arc Resistance	183	sec	ASTM D495
Coefficient of Thermal Expansion	4.3e-05	per °C	ASTM E831
Comparative Tracking Index	179	V	ASTM D3638
Compressive Strength	182	MPa	ASTM D695
Deflection Temperature (at 1.82MPa)	212	°C	ASTM D648
Dielectric Strength (Short Time)	9.6	kV/mm	ASTM D149
Dissipation Factor (at 1MHz)	0.087	—	ASTM D150
Flexural Modulus	9792	MPa	ASTM D790
Flexural Strength	93.5	MPa	ASTM D790
Heat Resistance	204	°C	ASTM D794
Impact Strength (Drop Ball)	116	J/m	Plenco
Impact Strength (Notched, Izod)	19.4	J/m	ASTM D256
Impact Strength (Notched, Charpy)	21.8	J/m	ASTM D256
Mold Shrinkage *	0.0043	m/m	ASTM D6289
Oxygen Index	28.1	%	ASTM D2863
Permittivity (at 1MHz)	6.2	—	ASTM D150
Post Shrinkage (at 120°C, 72hr)	0.21	%	ASTM D6289
Rockwell Hardness	82	E-Scale	ASTM D785
Specific Gravity	1.59	—	ASTM D792
Tensile Elongation	0.6	%	ASTM D638
Tensile Modulus	10183	MPa	ASTM D638
Tensile Strength	52	MPa	ASTM D638
Thermal Conductivity (at 100°C)	0.56	W/m/°C	ASTM E1461
UL Flammability (at 1.5mm)	V-0	—	UL 94
Volume Resistivity	210000000000	ohm·cm	ASTM D257
Water Absorption	0.13	%	ASTM D570

Regulatory & Compliance

Certifications & Compliance

UL 94