- Chemical Family
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Technologies
Features & Benefits
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Compression Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.63 | g/cm³ | ASTM D1895 |
Arc Resistance | 142 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.3e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 171 | V | ASTM D3638 |
Compressive Strength | 199 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 166 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 10.8 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.065 | — | ASTM D150 |
Flexural Modulus | 7848 | MPa | ASTM D790 |
Flexural Strength | 86 | MPa | ASTM D790 |
Heat Resistance | 203 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 98 | J/m | Plenco |
Impact Strength (Notched, Izod) | 16.5 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 17.4 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0081 | m/m | ASTM D6289 |
Oxygen Index | 30.6 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.2 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.31 | % | ASTM D6289 |
Rockwell Hardness | 85 | E-Scale | ASTM D785 |
Specific Gravity | 1.47 | — | ASTM D792 |
Tensile Elongation | 0.8 | % | ASTM D638 |
Tensile Modulus | 8679 | MPa | ASTM D638 |
Tensile Strength | 57 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.44 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-1 | — | UL 94 |
Volume Resistivity | 360000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.23 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.62 | g/cm³ | ASTM D1895 |
Arc Resistance | 157 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.3e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 161 | V | ASTM D3638 |
Compressive Strength | 206 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 192 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 11.9 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.044 | — | ASTM D150 |
Flexural Modulus | 8192 | MPa | ASTM D790 |
Flexural Strength | 78.3 | MPa | ASTM D790 |
Heat Resistance | 204 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 95 | J/m | Plenco |
Impact Strength (Notched, Izod) | 15.9 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 19.9 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0036 | m/m | ASTM D6289 |
Oxygen Index | 30.6 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.6 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.17 | % | ASTM D6289 |
Rockwell Hardness | 88 | E-Scale | ASTM D785 |
Specific Gravity | 1.47 | — | ASTM D792 |
Tensile Elongation | 0.6 | % | ASTM D638 |
Tensile Modulus | 8534 | MPa | ASTM D638 |
Tensile Strength | 53 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.44 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-1 | — | UL 94 |
Volume Resistivity | 3200000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.21 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.62 | g/cm³ | ASTM D1895 |
Arc Resistance | 137 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.3e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 163 | V | ASTM D3638 |
Compressive Strength | 207 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 192 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 11.1 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.058 | — | ASTM D150 |
Flexural Modulus | 8600 | MPa | ASTM D790 |
Flexural Strength | 94.1 | MPa | ASTM D790 |
Heat Resistance | 207 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 108 | J/m | Plenco |
Impact Strength (Notched, Izod) | 17.5 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 20.5 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0048 | m/m | ASTM D6289 |
Oxygen Index | 30.6 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.8 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.21 | % | ASTM D6289 |
Rockwell Hardness | 89 | E-Scale | ASTM D785 |
Specific Gravity | 1.48 | — | ASTM D792 |
Tensile Elongation | 0.8 | % | ASTM D638 |
Tensile Modulus | 9256 | MPa | ASTM D638 |
Tensile Strength | 60 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.44 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-1 | — | UL 94 |
Volume Resistivity | 13000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.2 | % | ASTM D570 |
Regulatory & Compliance