Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Technologies
Features & Benefits
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.61 | g/cm³ | ASTM D1895 |
Arc Resistance | 181 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 3.5e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 188 | V | ASTM D3638 |
Compressive Strength | 141 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 204 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 9.1 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.148 | — | ASTM D150 |
Flexural Modulus | 8787 | MPa | ASTM D790 |
Flexural Strength | 80 | MPa | ASTM D790 |
Heat Resistance | 203 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 148 | J/m | Plenco |
Impact Strength (Notched, Izod) | 19.7 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 20.6 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0051 | m/m | ASTM D6289 |
Oxygen Index | 33 | % | ASTM D2863 |
Permittivity (at 1MHz) | 6.6 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.33 | % | ASTM D6289 |
Rockwell Hardness | 58 | E-Scale | ASTM D785 |
Specific Gravity | 1.59 | — | ASTM D792 |
Tensile Elongation | 0.9 | % | ASTM D638 |
Tensile Modulus | 9924 | MPa | ASTM D638 |
Tensile Strength | 54 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.55 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-1 | — | UL 94 |
Volume Resistivity | 1700000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.38 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.61 | g/cm³ | ASTM D1895 |
Arc Resistance | 183 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 3.5e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 195 | V | ASTM D3638 |
Compressive Strength | 170 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 235 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 8.5 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.104 | — | ASTM D150 |
Flexural Modulus | 9664 | MPa | ASTM D790 |
Flexural Strength | 89.9 | MPa | ASTM D790 |
Heat Resistance | 204 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 153 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 24.5 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 25.7 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0036 | m/m | ASTM D6289 |
Oxygen Index | 33 | % | ASTM D2863 |
Permittivity (at 1MHz) | 7.5 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.32 | % | ASTM D6289 |
Rockwell Hardness | 71 | E-Scale | ASTM D785 |
Specific Gravity | 1.59 | — | ASTM D792 |
Tensile Elongation | 1 | % | ASTM D638 |
Tensile Modulus | 9990 | MPa | ASTM D638 |
Tensile Strength | 61 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.55 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-1 | — | UL 94 |
Volume Resistivity | 1500000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.46 | % | ASTM D570 |