Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Technologies
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
Properties
- Color
- Flame Rating
- Physical Form
- Processing Information (Injection Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.6 | g/cm³ | ASTM D1895 |
Arc Resistance | 106 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 4.9e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 164 | V | ASTM D3638 |
Compressive Strength | 182 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 154 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 10 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.052 | — | ASTM D150 |
Flexural Modulus | 6517 | MPa | ASTM D790 |
Flexural Strength | 69.6 | MPa | ASTM D790 |
Heat Resistance | 185 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 191 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 22.8 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 25.2 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0088 | m/m | ASTM D6289 |
Oxygen Index | 27.1 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.39 | % | ASTM D6289 |
Rockwell Hardness | 78 | E-Scale | ASTM D785 |
Specific Gravity | 1.4 | — | ASTM D792 |
Tensile Elongation | 0.8 | % | ASTM D638 |
Tensile Modulus | 8008 | MPa | ASTM D638 |
Tensile Strength | 51 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.4 | W/m/°C | ASTM E1461 |
UL Flammability (at 6mm) | V-0 | — | UL 94 |
Volume Resistivity | 2100000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.54 | % | ASTM D570 |