Properties
- Color
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.55 | g/cm³ | ASTM D1895 |
Arc Resistance | 120 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.7e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 151 | V | ASTM D3638 |
Compressive Strength | 187 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 148 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 7.5 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.065 | — | ASTM D150 |
Flexural Modulus | 6389 | MPa | ASTM D790 |
Flexural Strength | 68.2 | MPa | ASTM D790 |
Heat Resistance | 187 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 140 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 19.3 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 20.8 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0105 | m/m | ASTM D6289 |
Oxygen Index | 27.2 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.4 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.47 | % | ASTM D6289 |
Rockwell Hardness | 80 | E-Scale | ASTM D785 |
Specific Gravity | 1.37 | — | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 8067 | MPa | ASTM D638 |
Tensile Strength | 49 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.35 | W/m/°C | ASTM E1461 |
UL Flammability (at 6mm) | V-0 | — | UL 94 |
Volume Resistivity | 200000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.43 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.53 | g/cm³ | ASTM D1895 |
Arc Resistance | 93 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.7e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 160 | V | ASTM D3638 |
Compressive Strength | 197 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 166 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 9.7 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.061 | — | ASTM D150 |
Flexural Modulus | 6853 | MPa | ASTM D790 |
Flexural Strength | 67.1 | MPa | ASTM D790 |
Heat Resistance | 192 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 155 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 23.1 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 23.2 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0084 | m/m | ASTM D6289 |
Oxygen Index | 27.2 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.4 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.41 | % | ASTM D6289 |
Rockwell Hardness | 84 | E-Scale | ASTM D785 |
Specific Gravity | 1.37 | — | ASTM D792 |
Tensile Elongation | 0.6 | % | ASTM D638 |
Tensile Modulus | 7908 | MPa | ASTM D638 |
Tensile Strength | 43 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.35 | W/m/°C | ASTM E1461 |
UL Flammability (at 6mm) | V-0 | — | UL 94 |
Volume Resistivity | 200000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.43 | % | ASTM D570 |
Regulatory & Compliance
- Certifications & Compliance