Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Technologies
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Compression Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.57 | g/cm³ | ASTM D1895 |
Arc Resistance | 120 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.7e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 164 | V | ASTM D3638 |
Compressive Strength | 169 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 164 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 9.2 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.062 | — | ASTM D150 |
Flexural Modulus | 5808 | MPa | ASTM D790 |
Flexural Strength | 55.1 | MPa | ASTM D790 |
Heat Resistance | 187 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 218 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 30.5 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 31.7 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0086 | m/m | ASTM D6289 |
Oxygen Index | 24.2 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.6 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.39 | % | ASTM D6289 |
Rockwell Hardness | 73 | E-Scale | ASTM D785 |
Specific Gravity | 1.38 | — | ASTM D792 |
Tensile Elongation | 0.8 | % | ASTM D638 |
Tensile Modulus | 6941 | MPa | ASTM D638 |
Tensile Strength | 43 | MPa | ASTM D638 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 100000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.49 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.55 | g/cm³ | ASTM D1895 |
Arc Resistance | 120 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.7e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 162 | V | ASTM D3638 |
Compressive Strength | 146 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 178 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 12.3 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.048 | — | ASTM D150 |
Flexural Modulus | 7610 | MPa | ASTM D790 |
Flexural Strength | 76.7 | MPa | ASTM D790 |
Heat Resistance | 175 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 417 | J/m | Plenco |
Impact Strength (Notched, Izod) | 40.8 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 41.3 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0026 | m/m | ASTM D6289 |
Oxygen Index | 24.2 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.7 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.14 | % | ASTM D6289 |
Rockwell Hardness | 70 | E-Scale | ASTM D785 |
Specific Gravity | 1.39 | — | ASTM D792 |
Tensile Elongation | 0.4 | % | ASTM D638 |
Tensile Modulus | 8620 | MPa | ASTM D638 |
Tensile Strength | 34 | MPa | ASTM D638 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 600000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.6 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.47 | g/cm³ | ASTM D1895 |
Arc Resistance | 133 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.7e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 150 | V | ASTM D3638 |
Compressive Strength | 179 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 163 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 8.3 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.074 | — | ASTM D150 |
Flexural Modulus | 6737 | MPa | ASTM D790 |
Flexural Strength | 67 | MPa | ASTM D790 |
Heat Resistance | 187 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 312 | J/m | Plenco |
Impact Strength (Notched, Izod) | 28.4 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 29.1 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0091 | m/m | ASTM D6289 |
Oxygen Index | 24.2 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.3 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.29 | % | ASTM D6289 |
Rockwell Hardness | 76 | E-Scale | ASTM D785 |
Specific Gravity | 1.4 | — | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 6852 | MPa | ASTM D638 |
Tensile Strength | 43 | MPa | ASTM D638 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 170000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.37 | % | ASTM D570 |