Properties
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Compression Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.52 | g/cm³ | ASTM D1895 |
Arc Resistance | 120 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.8e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 158 | V | ASTM D3638 |
Compressive Strength | 213 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 150 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 10.8 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.047 | — | ASTM D150 |
Flexural Modulus | 6980 | MPa | ASTM D790 |
Flexural Strength | 86 | MPa | ASTM D790 |
Heat Resistance | 196 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 115 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 18.3 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 18.8 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0111 | m/m | ASTM D6289 |
Oxygen Index | 24.9 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.5 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.36 | % | ASTM D6289 |
Rockwell Hardness | 88 | E-Scale | ASTM D785 |
Specific Gravity | 1.37 | — | ASTM D792 |
Tensile Elongation | 0.9 | % | ASTM D638 |
Tensile Modulus | 8148 | MPa | ASTM D638 |
Tensile Strength | 62 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.36 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 81000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.35 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.51 | g/cm³ | ASTM D1895 |
Arc Resistance | 120 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.8e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 171 | V | ASTM D3638 |
Compressive Strength | 215 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 176 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 15.6 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.04 | — | ASTM D150 |
Flexural Modulus | 8806 | MPa | ASTM D790 |
Flexural Strength | 98.7 | MPa | ASTM D790 |
Heat Resistance | 194 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 171 | J/m | Plenco |
Impact Strength (Notched, Izod) | 23.3 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 24.3 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0038 | m/m | ASTM D6289 |
Oxygen Index | 24.9 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.7 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.16 | % | ASTM D6289 |
Rockwell Hardness | 90 | E-Scale | ASTM D785 |
Specific Gravity | 1.38 | — | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 8877 | MPa | ASTM D638 |
Tensile Strength | 54 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.36 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 2200000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.5 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.52 | g/cm³ | ASTM D1895 |
Arc Resistance | 126 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.8e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 157 | V | ASTM D3638 |
Compressive Strength | 221 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 166 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 11.4 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.05 | — | ASTM D150 |
Flexural Modulus | 7479 | MPa | ASTM D790 |
Flexural Strength | 81.8 | MPa | ASTM D790 |
Heat Resistance | 200 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 120 | J/m | Plenco |
Impact Strength (Notched, Izod) | 20 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 20.3 | J/m | ASTM D256 |
Mold Shrinkage * | 0.007 | m/m | ASTM D6289 |
Oxygen Index | 24.9 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.7 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.25 | % | ASTM D6289 |
Rockwell Hardness | 91 | E-Scale | ASTM D785 |
Specific Gravity | 1.37 | — | ASTM D792 |
Tensile Elongation | 0.8 | % | ASTM D638 |
Tensile Modulus | 7763 | MPa | ASTM D638 |
Tensile Strength | 52 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.36 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | HB | — | UL 94 |
Volume Resistivity | 560000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.3 | % | ASTM D570 |