Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Technologies
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Compression Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.62 | g/cm³ | ASTM D1895 |
Arc Resistance | 176 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 4.0e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 180 | V | ASTM D3638 |
Compressive Strength | 156 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 186 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 8.1 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.168 | — | ASTM D150 |
Flexural Modulus | 7251 | MPa | ASTM D790 |
Flexural Strength | 76.9 | MPa | ASTM D790 |
Heat Resistance | 204 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 126 | J/m | Plenco |
Impact Strength (Notched, Izod) | 18.1 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 19.6 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0062 | m/m | ASTM D6289 |
Oxygen Index | 30.6 | % | ASTM D2863 |
Permittivity (at 1MHz) | 6.9 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.42 | % | ASTM D6289 |
Rockwell Hardness | 57 | E-Scale | ASTM D785 |
Specific Gravity | 1.52 | — | ASTM D792 |
Tensile Elongation | 1.1 | % | ASTM D638 |
Tensile Modulus | 7979 | MPa | ASTM D638 |
Tensile Strength | 53 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.46 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-1 | — | UL 94 |
Volume Resistivity | 1000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.44 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.6 | g/cm³ | ASTM D1895 |
Arc Resistance | 183 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 4.0e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 188 | V | ASTM D3638 |
Compressive Strength | 177 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 216 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 13.2 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.051 | — | ASTM D150 |
Flexural Modulus | 8599 | MPa | ASTM D790 |
Flexural Strength | 74.3 | MPa | ASTM D790 |
Heat Resistance | 207 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 110 | J/m | Plenco |
Impact Strength (Notched, Izod) | 18.9 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 20.8 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0037 | m/m | ASTM D6289 |
Oxygen Index | 30.6 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.8 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.38 | % | ASTM D6289 |
Rockwell Hardness | 72 | E-Scale | ASTM D785 |
Specific Gravity | 1.54 | — | ASTM D792 |
Tensile Elongation | 0.8 | % | ASTM D638 |
Tensile Modulus | 9359 | MPa | ASTM D638 |
Tensile Strength | 54 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.46 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-1 | — | UL 94 |
Volume Resistivity | 16000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.41 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.6 | g/cm³ | ASTM D1895 |
Arc Resistance | 180 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 4.0e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 175 | V | ASTM D3638 |
Compressive Strength | 182 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 230 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 11.1 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.073 | — | ASTM D150 |
Flexural Modulus | 8658 | MPa | ASTM D790 |
Flexural Strength | 90.5 | MPa | ASTM D790 |
Heat Resistance | 203 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 126 | J/m | Plenco |
Impact Strength (Notched, Izod) | 20.7 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 21.9 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0027 | m/m | ASTM D6289 |
Oxygen Index | 30.6 | % | ASTM D2863 |
Permittivity (at 1MHz) | 6.5 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.27 | % | ASTM D6289 |
Rockwell Hardness | 76 | E-Scale | ASTM D785 |
Specific Gravity | 1.53 | — | ASTM D792 |
Tensile Elongation | 0.9 | % | ASTM D638 |
Tensile Modulus | 8563 | MPa | ASTM D638 |
Tensile Strength | 59 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.46 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-1 | — | UL 94 |
Volume Resistivity | 2800000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.39 | % | ASTM D570 |