Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Technologies
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Physical Form
- Processing Information (Injection Molding)
- Processing Information (Transfer Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.67 | g/cm³ | ASTM D1895 |
Arc Resistance | 184 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 3.8e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 192 | V | ASTM D3638 |
Compressive Strength | 155 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 263 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 13.5 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.039 | — | ASTM D150 |
Flexural Modulus | 10714 | MPa | ASTM D790 |
Flexural Strength | 77.9 | MPa | ASTM D790 |
Heat Resistance | 187 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 178 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 30.8 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 34.3 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0045 | m/m | ASTM D6289 |
Oxygen Index | 46.4 | % | ASTM D2863 |
Permittivity (at 1MHz) | 4.9 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.1 | % | ASTM D6289 |
Rockwell Hardness | 81 | E-Scale | ASTM D785 |
Specific Gravity | 1.72 | — | ASTM D792 |
Tensile Elongation | 0.5 | % | ASTM D638 |
Tensile Modulus | 12311 | MPa | ASTM D638 |
Tensile Strength | 45 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.58 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-0 | — | UL 94 |
Volume Resistivity | 2200000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.12 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.71 | g/cm³ | ASTM D1895 |
Arc Resistance | 184 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 3.8e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 181 | V | ASTM D3638 |
Compressive Strength | 168 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 280 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 14.3 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.033 | — | ASTM D150 |
Flexural Modulus | 12790 | MPa | ASTM D790 |
Flexural Strength | 102.4 | MPa | ASTM D790 |
Heat Resistance | 225 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 227 | J/m | Plenco |
Impact Strength (Notched, Izod) | 57.1 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 62 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0014 | m/m | ASTM D6289 |
Oxygen Index | 46.4 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.07 | % | ASTM D6289 |
Rockwell Hardness | 78 | E-Scale | ASTM D785 |
Specific Gravity | 1.78 | — | ASTM D792 |
Tensile Elongation | 0.6 | % | ASTM D638 |
Tensile Modulus | 13086 | MPa | ASTM D638 |
Tensile Strength | 57 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.58 | W/m/°C | ASTM E1461 |
UL Flammability (at 1.5mm) | V-0 | — | UL 94 |
Volume Resistivity | 1300000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.09 | % | ASTM D570 |
Regulatory & Compliance
- Certifications & Compliance