Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Technologies
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
Properties
- Color
- Flame Rating
- Processing Information (Injection Molding)
- Processing Information (Compression Molding)
Value | Units | Test Method / Conditions | |
Apparent Density | 0.59 | g/cm³ | ASTM D1895 |
Arc Resistance | 126 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.7e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 165 | V | ASTM D3638 |
Compressive Strength | 188 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 152 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 9.1 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.062 | — | ASTM D150 |
Flexural Modulus | 6848 | MPa | ASTM D790 |
Flexural Strength | 68.2 | MPa | ASTM D790 |
Heat Resistance | 190 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 140 | J/m | Plenco |
Impact Strength (Notched, Charpy) | 18.6 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 20.5 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0097 | m/m | ASTM D6289 |
Oxygen Index | 26.1 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.4 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.45 | % | ASTM D6289 |
Rockwell Hardness | 82 | E-Scale | ASTM D785 |
Specific Gravity | 1.38 | — | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 8445 | MPa | ASTM D638 |
Tensile Strength | 49 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.38 | W/m/°C | ASTM E1461 |
UL Flammability (at 5.1mm) | V-0 | — | UL 94 |
Volume Resistivity | 400000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.36 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Apparent Density | 0.6 | g/cm³ | ASTM D1895 |
Arc Resistance | 120 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.7e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 179 | V | ASTM D3638 |
Compressive Strength | 191 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 179 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 12.3 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.046 | — | ASTM D150 |
Flexural Modulus | 8410 | MPa | ASTM D790 |
Flexural Strength | 76.4 | MPa | ASTM D790 |
Heat Resistance | 187 | °C | ASTM D794 |
Impact Strength (Drop Ball) | 173 | J/m | Plenco |
Impact Strength (Notched, Izod) | 23.7 | J/m | ASTM D256 |
Impact Strength (Notched, Charpy) | 24.5 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0043 | m/m | ASTM D6289 |
Oxygen Index | 26.1 | % | ASTM D2863 |
Permittivity (at 1MHz) | 5.1 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0.27 | % | ASTM D6289 |
Rockwell Hardness | 78 | E-Scale | ASTM D785 |
Specific Gravity | 1.4 | — | ASTM D792 |
Tensile Elongation | 0.6 | % | ASTM D638 |
Tensile Modulus | 9097 | MPa | ASTM D638 |
Tensile Strength | 46 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.38 | W/m/°C | ASTM E1461 |
UL Flammability (at 5.1mm) | V-0 | — | UL 94 |
Volume Resistivity | 1000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.64 | % | ASTM D570 |
Regulatory & Compliance
- Certifications & Compliance