Value | Units | Test Method / Conditions | |
Arc Resistance | 185 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 4.8e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 600 | V | ASTM D3638 |
Compressive Strength | 137 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 264 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 11.7 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.025 | — | ASTM D150 |
Flexural Modulus | 15306 | MPa | ASTM D790 |
Flexural Strength | 97.7 | MPa | ASTM D790 |
Heat Resistance | 224 | °C | ASTM D794 |
Impact Strength (Notched, Charpy) | 231.5 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 237.4 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0013 | m/m | ASTM D6289 |
Permittivity (at 1MHz) | 5 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0 | % | ASTM D6289 |
Rockwell Hardness | 55 | E-Scale | ASTM D785 |
Specific Gravity | 2.02 | — | ASTM D792 |
Tensile Elongation | 0.5 | % | ASTM D638 |
Tensile Modulus | 17098 | MPa | ASTM D638 |
Tensile Strength | 43 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.76 | W/m/°C | ASTM E1461 |
UL Flammability | HB | — | UL 94 |
Volume Resistivity | 7900000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.08 | % | ASTM D570 |