Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Reinforcement Material
- Composite Materials Functions
- Technologies
Features & Benefits
- Labeling Claims
Applications & Uses
- Applications
- Composites End Use
- Composites Processing Methods
Properties
- Flame Rating
- Physical Form
- Processing Information (Compression Molding)
Value | Units | Test Method / Conditions | |
Arc Resistance | 191 | sec | ASTM D495 |
Coefficient of Thermal Expansion | 5.3e-05 | per °C | ASTM E831 |
Comparative Tracking Index | 600 | V | ASTM D3638 |
Compressive Strength | 141 | MPa | ASTM D695 |
Deflection Temperature (at 1.82MPa) | 270 | °C | ASTM D648 |
Dielectric Strength (Short Time) | 13.3 | kV/mm | ASTM D149 |
Dissipation Factor (at 1MHz) | 0.02 | — | ASTM D150 |
Flexural Modulus | 12839 | MPa | ASTM D790 |
Flexural Strength | 137.1 | MPa | ASTM D790 |
Heat Resistance | 220 | °C | ASTM D794 |
Impact Strength (Notched, Charpy) | 469.6 | J/m | ASTM D256 |
Impact Strength (Notched, Izod) | 471.6 | J/m | ASTM D256 |
Mold Shrinkage * | 0.0027 | m/m | ASTM D6289 |
Permittivity (at 1MHz) | 4.4 | — | ASTM D150 |
Post Shrinkage (at 120°C, 72hr) | 0 | % | ASTM D6289 |
Rockwell Hardness | 51 | E-Scale | ASTM D785 |
Specific Gravity | 1.85 | — | ASTM D792 |
Tensile Elongation | 0.7 | % | ASTM D638 |
Tensile Modulus | 13888 | MPa | ASTM D638 |
Tensile Strength | 54 | MPa | ASTM D638 |
Thermal Conductivity (at 100°C) | 0.93 | W/m/°C | ASTM E1461 |
UL Flammability | V-0 | — | UL 94 |
UL Flammability (at 1.5mm) | 5VA | — | UL 94 |
Volume Resistivity | 37000000000000000 | ohm·cm | ASTM D257 |
Water Absorption | 0.1 | % | ASTM D570 |
Regulatory & Compliance
- Certifications & Compliance
- Chemical Inventories