Products

OPTIM® E-156 is a maleic anhydride modified high density polyethylene. It is used for a variety of applications where adhesion improvements or compatibilsation is required.

OPTIM® E-118 is a maleic anhydride modified linear low-density polyethylene. It has been designed to promote adhesion between carrier polymer and high loading of mineral fillers in HFFR cable compounds. Without this coupling agent, it is not possible to achieve the required mechanical properties in the cable compound.

BindEX E-160 is a maleic anhydride modified linear low density polyethylene adhesive resin. It can be processed within different extrusion and co-extrusion technologies designed to process polyolefins. It is especially designed to combine aluminum sheets with polymer core in Aluminum composite panels, using extrusion coating process.

OPTIM® E-152 is a maleic anhydride modified polyethylene with additional ester groups. It is used as compatibilizer between polar and non-polar polymers. It also acts as coupling agent to improve adhesion of mineral fillers and polymer matrix.

OPTIM® R-658 is a maleic anhydride modified elastomeric resin in granular form. It can be processed using plastics molding and extrusion techniques designed for polyolefins. The grafted polar groups on otherwise poyolefinic chains make it compatible with other polar and non-polar polymers. This affords many possibilities of extending base polymer properties like wettablity and toughening.

BindEX E-165 is a modified linear low density polyethylene adhesive resin designed for use in adhesive film for making Aluminum Composite Panels (ACP). The chemical modification provides excellent adhesion to both polyethylene and aluminum substrates. It is preferably used as outer layer in 3- layer coextruded blown film structure. It is this layer which faces aluminum sheet during lamination process. It can be processed on normal extruders used for processing of polyethylenes.

NOVIS P-492 is a high flow maleic anhydride grafted Polypropylene material. Presence of maleic anhydride moieties on PP chains make NOVIS P-492 significantly polar versus plain PP. This makes it useful as adhesion promotor when added to a polyolefin based hot melt composition. Being a low molecular weight polymer, it blends well with other ingredients in the composition. NOVIS P-492 is a polymer with narrow molecular weight distribution, which can impart higher mechanical strength compared with that provided by conventional waxes.

BindEX E-186 is a maleic anhydride modified metallocene based linear low density polyethylene. With advanced anhydride grafting technology, this grade creates superb adhesion to EVOH, PA and PE, while maintaining excellent process ability.

MB-80 is an adhesive resin based on modified polyethylene. It can be used to produce a three-layer low temperature adhesive film, for manufacture of Aluminum Composite Panels (ACP). The chemical modification provides excellent adhesion to both polyethylene and aluminum substrates. It is preferably used as outer layer in 3- layer coextruded blown film structure. It is this layer with MB-80, which faces aluminum sheet during ACP manufacturing process. It can be processed on normal extruders used for making 3-layer polyethylene films.

OPTIM® P-408 is a maleic anhydride modified homopolymer polypropylene. The grafting operation of the polypropylene backbone is achieved using a new technology that allows high grafting efficiency and low polymer scission.

OPTIM® E-151 is a maleic anhydride modified polyethylene with additional ester groups. It is used as compatibilizer between polar and non-polar polymers. It also acts as coupling agent to improve adhesion of mineral fillers and polymer matrix.

OPTIM® E-119 is a maleic anhydride modified linear low density polyethylene. It is used to improve adhesion of HFFR fillers such as Magnesium Hydroxide [Mg(OH)2] & Alumina Trihydrate (ATH) and the polymer matrix.