Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Technologies
- Product Families
Properties
- Mechanical Properties
- Typical Properties
- Thermal Properties
- Processing Properties
- Electrical Properties and Flammability
Value | Units | Test Method / Conditions | |
Tensile Modulus | 1700 | MPa | ISO 527-2 |
Young Modulus | 2000 | MPa | ISO 527-2 |
Tensile Strength at Break | 45 | MPa | ISO 527-2 |
Tensile Strength at Yield | 30 | Mpa | ISO 527-2 |
Elongation at Break | min. 10 | % | ISO 527-2 |
Elongation at Yield | 2,0 | % | ISO 527-2 |
Flexural Modulus | 2150 | Mpa | ISO 178 |
Flexural Strength | 70 | Mpa | ISO 178 |
Charpy notched (23°C) | 6,0 | kJ/m2 | ISO 179 |
Charpy notched (-30°C) | 5,5 | kJ/m2 | ISO 179 |
Izod notched impact (23°C) | 4,5 | kJ/m2 | ISO 180/1A |
Izod unnotched impact (-30°C) | 4,0 | kJ/m2 | ISO 180/1U |
Value | Units | Test Method / Conditions | |
Density | 1.52 | g/cm³ | ISO 1183 |
Water Absorption (Saturation in water 23°C) | 0,60 | % | ISO 62 |
Water absorption,(Equilibrium value) (50% RH, 23°C) | 0,18 | % | ISO 62 |
Value | Units | Test Method / Conditions | |
MFR/MFI(Melt Flow Rate) (190 °C 2,16 kg) | 5 - 12 | g / 10 min | ISO 1133 |
VICAT (50 N - 50 °C/h) | 145 | °C | ISO 306 |
HDT A (1.80 Mpa) | 86 | °C | ISO 75-2 |
HDT B (0.45 Mpa) | 126 | °C | ISO 75-2 |
Coeff.of linear therm expansion | 13,0 | E-5/oC | ISO 11359 |
Value | Units | Test Method / Conditions | |
Melting Temperature, DSC | 165 | °C | ISO 11357-1/-3 |
Melt Temperature, for processing | 180 - 210 | °C | — |
Cylinder Settings | 180 - 230 | °C | — |
Screw Design | Universal Type | — | — |
Mould Temperature, injection moulding | 40 - 60 | °C | — |
Moulding shrinkage (parallel,2mm) | 2,0 | % | ISO 294-4 |
Moulding shrinkage (normal,2mm) | 2,0 | % | ISO 294-4 |
Value | Units | Test Method / Conditions | |
Flame Rating (1.6 mm) | HB | class | UL94 |
Volume Resistivity | 1.00E+14 | Ohm.m | IEC 60093 |
Surface Resistivity | 10000000000000000 | ohm | IEC 60093 |