Properties
- Color
- Flame Rating
- Mechanical Properties
- Typical Properties
- Thermal Properties
- Processing Properties
- Electrical Properties and Flammability
Value | Units | Test Method / Conditions | |
Tensile Modulus | 1300 | MPa | ISO 527-2 |
Young Modulus | 1750 | MPa | ISO 527-2 |
Tensile Strength at Break | 50 | MPa | ISO 527-2 |
Tensile Strength at Yield | 35 | Mpa | ISO 527-2 |
Elongation at Break | min. 30 | % | ISO 527-2 |
Elongation at Yield | 4,5 | % | ISO 527-2 |
Flexural Modulus | 2250 | Mpa | ISO 178 |
Flexural Strength | 65 | Mpa | ISO 178 |
Charpy notched (23°C) | 12,0 | kJ/m2 | ISO 179 |
Charpy notched (-30°C) | 8,0 | kJ/m2 | ISO 179 |
Izod notched impact (23°C) | 14,0 | kJ/m2 | ISO 180/1A |
Izod unnotched impact (-30°C) | 12,0 | kJ/m2 | ISO 180/1U |
Value | Units | Test Method / Conditions | |
Density | 1.37 | g/cm³ | ISO 1183 |
Water Absorption (Saturation in water 23°C) | 0,80 | % | ISO 62 |
Water absorption,(Equilibrium value) (50% RH, 23°C) | 0,25 | % | ISO 62 |
Value | Units | Test Method / Conditions | |
MFR/MFI(Melt Flow Rate) (190 °C 2,16 kg) | 5 - 12 | g / 10 min | ISO 1133 |
MVR(Melt Volume Rate) (190 °C 2,16 kg) | 4,5 - 10,5 | cm3/10 min | ISO 1133 |
VICAT (50 N - 50 °C/h) | 126 | °C | ISO 306 |
HDT A (1.80 Mpa) | 77 | °C | ISO 75-2 |
HDT B (0.45 Mpa) | 135 | °C | ISO 75-2 |
Ball Pressure Test | 72,4 | mm | IEC 60695-10-2 |
Shore-Sertlik (D) | 1,1 | N | ISO 868 |
Coeff.of linear therm expansion , parallel | 1,1 | E-4/oC | ISO 11359-2 |
Coeff.of linear therm expansion , normal | 13,0 | E-5/oC | ISO 11359 |
Value | Units | Test Method / Conditions | |
Melting Temperature, DSC | 165 | °C | ISO 11357-1/-3 |
Melt Temperature, for processing | 180 - 210 | °C | — |
Cylinder Settings | 180 - 230 | °C | — |
Screw Design | Universal Type | — | — |
Mould Temperature, injection moulding | 40 - 60 | °C | — |
Moulding shrinkage (parallel,2mm) | 1,80 | % | ISO 294-4 |
Moulding shrinkage (normal,2mm) | 1,60 | % | ISO 294-4 |
Value | Units | Test Method / Conditions | |
Flame Rating (1.6 mm) | HB | class | UL94 |
Volume Resistivity | 1.00E+14 | Ohm.m | IEC 60093 |
Surface Resistivity | 10000000000000000 | ohm | IEC 60093 |