Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Applications & Uses
- Applications
- Composites Processing Methods
- Main application
- Cast
Properties
- Physical Form
- Appearance
- Clear rosé
- Mechanical Properties
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Barcol hardness | 45 | — | ASTM D2583-01 |
| Elongation at break | 2.6 | % | ASTM D638 |
| Heat deflection temperature (HDT) Stresses of 1820 kPa | 65 | °C | ASTM D648 |
| Heat deflection temperature (HDT) Stresses of 455 kPa | 77 | °C | — |
| Tensile modulus | 3800 | MPa | ASTM D638 |
| Tensile strength at break | 64 | MPa | ASTM D638 |
| Value | Units | Test Method / Conditions | |
| Acid Value (at 23°C) | max. 26 | mg KOH/g | UNI EN ISO 2114 |
| Monomer (at 23°C) | Styrene | — | — |
| Stability (in the dark at 23°C) | 6 months | — | Internal studies |
| Styrene content (at 23°C) | 36.0 - 38.0 | % w/w | V5 - 2010 (rif. UNI 9560) |
| Viscosity Brookfield (at 23°C) | 450 - 600 | mPa*s | V2 - 2010 (rif. UNI 8701/3) |
| Value | Units | Test Method / Conditions | |
| Gel time (at 23°C catalysis 1.5g of MEKP and 100g of liquid resin) | 4’30 - 6’30 | Min. | V1.1 - 2010 (rif. DIN 16945) |
| Gel time to peak exotherm (at 23°C catalysis 1.5g of MEKP and 100g of liquid resin) | 5’30 - 7’00 | Min. | V1.1 - 2010 (rif. DIN 16945) |
| Peak exotherm (at 23°C catalysis 1.5g of MEKP and 100g of liquid resin) | 180 - 195 | °C | V1.1 - 2010 (rif. DIN 16945) |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Packaging Type
- Delivery
- Bulk 20-27 tons max with 1100 kg IBC tank or IsoTank or 220 kg drums on 4 pallets