Properties
- Filler Content
- 13 - 17
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Processing Parameters
| Value | Units | Test Method / Conditions | |
| Moisture Content | max. 0.1 | % | — |
| Melt Flow Index - MFI (230°C/5 kg) | 8 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.2 - 0.4 | % | ISO 294-4 |
| Density | 1.13 | g/cm³ | ISO 1183/A |
| Molding Shrinkage - Across Flow | 0.2 - 0.4 | % | ISO 294-4 |
| Value | Units | Test Method / Conditions | |
| Tensile Strength | max. 42 | MPa | ISO 527-2 |
| Flexural Strength | max. 73 | MPa | ISO 178 |
| Elongation at Break | 4.5 | % | ASTM D 638 |
| Flexural Modulus (23°C) | 3700 | MPa | ISO 178 |
| Charpy Notched Impact Strength (23°C) | 7 | kJ/m² | ISO 179 |
| Value | Units | Test Method / Conditions | |
| Heat Distortion Temperature B (120°C/h at 455kPa) | 105 | °C | ISO 75/1 |
| Heat Distortion Temperature A (120°C/h at 1820kPa) | 95 | °C | ISO 75/1 |
| Vicat Softening Tempurature A (50°C/h at 9,81N) | 108 | °C | ISO 306 |
| Vicat Softening Tempurature B (50°C/h at 49,05N) | 103 | °C | ISO 306 |
| Value | Units | Test Method / Conditions | |
| Drying Temperature | 80 | °C | — |
| Peripherical Screw Speed | 400-600 | mm/s | — |
| Drying Time | 2 - 4 | h | — |
| Melt Temperature | 190 - 230 | °C | — |
| Mold Temperature | 60 - 80 | °C | — |
| Back Pressure | 60 - 100 | bar | — |