Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Plastics & Elastomers Processing Methods
Properties
- Filler Content
- 38 - 42
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Flammability
- Processing Parameters
| Value | Units | Test Method / Conditions | |
| Tensile Strength | max. 30 | MPa | ISO 527-2 |
| Flexural Strength | max. 50 | MPa | ISO 178 |
| Elongation at Yield | 6 | % | ASTM D 638 |
| Flexural Modulus (23°C) | 2800 | MPa | ISO 178 |
| Charpy Notched Impact Strength (23°C) | 3 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 15 | kJ/m² | ISO 179 |
| Value | Units | Test Method / Conditions | |
| Melt Flow Index - MFI (230°C/2.16kg) | 8 | g/10min | ISO 1133 |
| Density | 1.21 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.8 - 1.2 | % | ISO 294-4 |
| Molding Shrinkage - Across Flow | 0.8 - 1.2 | % | ISO 294-4 |
| Value | Units | Test Method / Conditions | |
| Vicat Softening Tempurature B (50°C/h at 49,05N) | 90 | °C | ISO 306 |
| Vicat Softening Tempurature A (50°C/h at 9,81N) | 150 | °C | ISO 306 |
| Heat Distortion Temperature A (120°C/h at 1820kPa) | 65 | °C | ISO 75/1 |
| Heat Distortion Temperature B (120°C/h at 455kPa) | 120 | °C | ISO 75/1 |
| Value | Units | Test Method / Conditions | |
| Glow Wire Flammability Index - GWFI (2 mm) | 750 | °C | IEC 60695-2-12 |
| Value | Units | Test Method / Conditions | |
| Drying Temperature | 70 - 80 | °C | - |
| Drying Time | 2 - 4 | h | - |
| Back Pressure | 60 - 100 | bar | - |
| Melt Temperature | 205 - 260 | °C | - |
| Mold Temperature | 40 - 80 | °C | - |
| Peripherical Screw Speed | 600 - 750 | mm/s | - |
Packaging & Availability
- Country Availability
- Regional Availability