Value | Units | Test Method / Conditions | |
Tensile Strength | max. 65 | MPa | ISO 527-2 |
Flexural Strength | max. 95 | MPa | ISO 178 |
Elongation at Yield | 9 | % | ASTM D 638 |
Flexural Modulus (23°C) | 2600 | MPa | ISO 178 |
Charpy Notched Impact Strength (23°C) | 8 | kJ/m² | ISO 179 |
Charpy Notched Impact Strength (-20°C) | 7 | kJ/m² | ISO 179 |
Value | Units | Test Method / Conditions | |
Melt Flow Index - MFI (190°C/2.16kg) | 9 | g/10min | ISO 1133 |
Density | 1.41 | g/cm³ | ISO 1183 |
Molding Shrinkage - Flow | 1.8 - 2.0 | % | ISO 294-4 |
Molding Shrinkage - Across Flow | 1.8 - 2.0 | % | ISO 294-4 |
Value | Units | Test Method / Conditions | |
Heat Distortion Temperature A (120°C/h at 1820kPa) | 104 | °C | ISO 75/1 |
Vicat Softening Tempurature B (50°C/h at 49,05N) | 151 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Peripherical Screw Speed | 150-450 | mm/s | — |
Mold Temperature | 70 - 110 | °C | — |
Drying Time | 2 - 4 | h | — |
Back Pressure | 60 - 100 | bar | — |
Melt Temperature | 190 - 210 | °C | — |
Drying Temperature | 70 - 90 | °C | — |