Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Applications & Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Processing Parameters
| Value | Units | Test Method / Conditions | |
| Tensile Strength | max. 80 | MPa | ISO 527-2 |
| Flexural Strength | max. 140 | MPa | ISO 178 |
| Elongation at Yield | 10 | % | ASTM D 638 |
| Flexural Modulus (23°C) | 3000 | MPa | ISO 178 |
| Charpy Notched Impact Strength (23°C) | 4 | kJ/m² | ISO 179 |
| Value | Units | Test Method / Conditions | |
| Melt Flow Index - MFI (230°C/5 kg) | 2 | g/10 min | ISO 1133 |
| Density | 1.19 | g/cm³ | ASTM D792 |
| Value | Units | Test Method / Conditions | |
| Vicat Softening Tempurature B (50°C/h at 49,05N) | 110 | °C | ISO 306 |
| Heat Distortion Temperature B (120°C/h at 455kPa) | 102 | °C | ISO 75/1 |
| Heat Distortion Temperature A (120°C/h at 1820kPa) | 82 | °C | ISO 75/1 |
| Vicat Softening Tempurature A (50°C/h at 9,81N) | 116 | °C | ISO 306 |
| Value | Units | Test Method / Conditions | |
| Drying Time | 2-3 | h | — |
| Mold Temperature | 50 - 80 | °C | — |
| Melt Temperature | 210 - 240 | °C | — |
| Back Pressure | 60 - 100 | bar | — |
| Drying Temperature | 75 - 80 | °C | — |
| Peripherical Screw Speed | 250 - 400 | mm/s | — |