Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Plastics & Elastomers Functions
- Technologies
- Product Families
- Processing Method
Injection Molding
- Additive
Flame Retardant
Features & Benefits
- Materials Features
- Features
- Flame Retardant
- High Impact Resistance
- High Viscosity
- Low Flow
- Medium Heat Resistance
- Self Extinguishing
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Composites Processing Methods
- Plastics & Elastomers Processing Methods
Properties
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Flammability
- Processing Information (Injection Molding)
- Impact Properties
- Hardness
| Value | Units | Test Method / Conditions | |
| Density | 1.21 | — | ASTM D792 |
| Melt Mass Flow Rate (at 300°C, 1.2 kg) | 5.0 - 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage (at 0.125 in, Flow) | 5.0E-3 to 7.0E-3 | in/in | ASTM D955 |
| Molding Shrinkage (at 0.125 in, Across Flow) | 5.0E-3 to 7.0E-3 | in/in | ASTM D955 |
| Specific Gravity | 1.21 | — | ASTM D792 |
| Outdoor Suitability | f1 | — | UL 746C |
| Value | Units | Test Method / Conditions | |
| Tensile Strength (at Yield, 0.125 in) | 9000 | psi | ASTM D638 |
| Tensile Strength (at Break, 0.125 in) | 8000 | psi | ASTM D638 |
| Tensile Elongation (at Yield, 0.125 in) | 7 | % | ASTM D638 |
| Tensile Elongation (at Break, 0.125 in) | 90 | % | ASTM D638 |
| Flexural Modulus (at 0.125 in) | 320000 | psi | ASTM D790 |
| Flexural Strength (at 0.125 in) | 13000 | psi | ASTM D790 |
| Value | Units | Test Method / Conditions | |
| Deflection Temperature Under Load (at 66 psi, 0.125 in, Unannealed) | 275 | °F | ASTM D648 |
| Deflection Temperature Under Load (at 264 psi, 0.125 in, Unannealed) | 265 | °F | ASTM D648 |
| Relative Thermal Index Electrical Property (at 0.06 in) | 257 | °F | UL 746 |
| Relative Thermal Index Electrical Property (at 0.12 in) | 257 | °F | UL 746 |
| Relative Thermal Index Impact Property (at 0.06 in) | 230 | °F | UL 746 |
| Relative Thermal Index Impact Property (at 0.12 in) | 230 | °F | UL 746 |
| Relative Thermal Index Strength Property (at 0.06 in) | 257 | °F | UL 746 |
| Relative Thermal Index Strength Property (at 0.12 in) | 257 | °F | UL 746 |
| Vicat Softening Temperature | 300 | °F | ASTM D1525 ² |
| Value | Units | Test Method / Conditions | |
| Volume Resistivity | 1.0e+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (at 0.0591 in) | 580 | V/mil | ASTM D149 |
| Arc Resistance (at 0.0591 in) | PLC 5 | — | ASTM D495 |
| Comparative Tracking Index (at 0.0591 in) | PLC 2 | — | UL 746 |
| High Amp Arc Ignition (at 0.06 in) | PLC 0 | — | UL 746 |
| High Amp Arc Ignition (at 0.12 in) | PLC 0 | — | UL 746 |
| High Voltage Arc Tracking Rate (at 0.0591 in) | PLC 3 | — | UL 746 |
| Hot Wire Ignition (at 0.06 in) | PLC 2 | — | UL 746 |
| Hot Wire Ignition (at 0.12 in) | PLC 2 | — | UL 746 |
| Value | Units | Test Method / Conditions | |
| Flame Rating (at 0.06 in) | V-0 | — | UL 94 |
| Flame Rating (at 0.12 in) | V-0, 5VA | — | UL 94 |
| Value | Units | Test Method / Conditions | |
| Drying Temperature | 245 - 255 | °F | — |
| Drying Time | 3.0 - 4.0 | hr | — |
| Front Temperature | 590 - 630 | °F | — |
| Middle Temperature | 570 - 610 | °F | — |
| Mold Temperature | 180 - 240 | °F | — |
| Rear Temperature | 550 - 590 | °F | — |
| Maximum Drying Time | 8 | hr | — |
| Processing Temperature (Melt) | 600 - 650 | °F | — |
| Value | Units | Test Method / Conditions | |
| Impact Strength (at 73°F, 0.125 in, Notched Izod) | 12 | ft·lb/in | ASTM D256 |
| Gardner Impact Strength (at 0.125 in) | min. 320 | in·lb | ASTM D3029 |
| Value | Units | Test Method / Conditions | |
| Rockwell Hardness (M-Scale) | 70 | — | ASTM D785 |
| Rockwell Hardness (R-Scale) | 118 | — | ASTM D785 |
Regulatory & Compliance
- Certifications & Compliance
- Quality Standards
- Agency Ratings & Compliance
RoHS Compliant
Packaging & Availability
- Regional Availability
- Availability
North America