Knowde Enhanced TDS
Identification & Functionality
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Processing Method
Injection Molding
- Additive
Flame Retardant
- Filler and Reinforcement
- Filler : Glass Fiber
- Reinforcement : 30% Filler by Weight
Features & Benefits
- Materials Features
- Features
- Flame Retardant
- High Heat Resistance
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Flammability
- Processing Information (Injection Molding)
- Impact Properties
- Hardness
Value | Units | Test Method / Conditions | |
Density | 1.51 | — | ASTM D792 |
Melt Mass Flow Rate (at 337°C, 6.6 kg) | 5.0 - 22 | g/10 min | ASTM D1238 |
Molding Shrinkage (Flow) | 1.0E-3 to 4.0E-3 | in/in | ASTM D955 |
Water Absorption (24 hrs) | 0.16 | % | ASTM D570 |
Water Absorption (at Equilibrium, 73°F) | 0.9 | % | ASTM D570 |
Specific Gravity | 1.51 | — | ASTM D792 |
Value | Units | Test Method / Conditions | |
Tensile Modulus (at 0.125 in) | 1350000 | psi | ASTM D638 |
Tensile Strength (at Yield, 0.125 in) | 23500 | psi | ASTM D638 |
Tensile Strength (at Break, 0.125 in) | 23500 | psi | ASTM D638 |
Tensile Elongation (at Break, 0.125 in) | 3 | % | ASTM D638 |
Flexural Modulus (at 0.125 in) | 1290000 | psi | ASTM D790 |
Flexural Strength (at 0.125 in) | 32000 | psi | ASTM D790 |
Value | Units | Test Method / Conditions | |
Deflection Temperature Under Load (at 66 psi, 0.125 in, Unannealed) | 412 | °F | ASTM D648 |
Deflection Temperature Under Load (at 264 psi, 0.125 in, Unannealed) | 410 | °F | ASTM D648 |
Coefficient of Linear Thermal Expansion (at -4 to 302°F, Flow) | 1.0e-05 | in/in/°F | ASTM E831 |
Coefficient of Linear Thermal Expansion (at -4 to 302°F, Transverse) | 2.3e-05 | in/in/°F | ASTM E831 |
Relative Thermal Index Electrical Property (at 0.06 in) | 221 | °F | UL 746 |
Relative Thermal Index Electrical Property (at 0.12 in) | 221 | °F | UL 746 |
Relative Thermal Index Impact Property (at 0.06 in) | 221 | °F | UL 746 |
Relative Thermal Index Impact Property (at 0.12 in) | 221 | °F | UL 746 |
Relative Thermal Index Strength Property (at 0.06 in) | 221 | °F | UL 746 |
Relative Thermal Index Strength Property (at 0.12 in) | 221 | °F | UL 746 |
Vicat Softening Temperature | 440 | °F | ASTM D1525 ² |
Value | Units | Test Method / Conditions | |
Volume Resistivity | 30000000000000000 | ohms·cm | ASTM D257 |
Dielectric Strength (at 0.0625 in, in Air) | 620 | V/mil | ASTM D149 |
Dielectric Strength (at 0.0625 in, in Oil) | 760 | V/mil | ASTM D149 |
Dielectric Constant (at 1 kHz) | 3.7 | — | ASTM D150 |
Dissipation Factor (at 1 kHz) | 0.0015 | — | ASTM D150 |
Dissipation Factor (at 2 GHz) | 0.0053 | — | ASTM D150 |
Value | Units | Test Method / Conditions | |
Flame Rating (at 0.06 in, All) | V-0 | — | UL 94 |
Flame Rating (at 0.12 in, All) | V-0 | — | UL 94 |
Value | Units | Test Method / Conditions | |
Drying Temperature | 290 - 300 | °F | — |
Drying Time | 4.0 - 6.0 | hr | — |
Front Temperature | 650 - 750 | °F | — |
Middle Temperature | 640 - 750 | °F | — |
Mold Temperature | 225 - 350 | °F | — |
Rear Temperature | 630 - 750 | °F | — |
Suggested Shot Size | 40 - 60 | % | — |
Maximum Drying Time | 8 | hr | — |
Suggested Maximum Moisture Content | 0.02 | % | — |
Processing Temperature (Melt) | 640 - 750 | °F | — |
Value | Units | Test Method / Conditions | |
Impact Strength (at 73°F, 0.125 in, Notched Izod) | 1.5 | ft·lb/in | ASTM D256 |
Impact Strength (at 73°F, 0.125 in, Unnotched Izod) | 8 | ft·lb/in | ASTM D4812 |
Impact Strength (at 73°F, 0.125 in, Reverse Notch Izod) | 8.7 | ft·lb/in | ASTM D256 |
Value | Units | Test Method / Conditions | |
Rockwell Hardness | 114 | — | ASTM D785 |
Regulatory & Compliance
- Certifications & Compliance
- Quality Standards
- Agency Ratings & Compliance
RoHS Compliant
Packaging & Availability
- Regional Availability
- Availability
North America