Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Processing Method
Injection Molding
- Additive
Lubricant
Features & Benefits
- Materials Features
- Features
- General Purpose
- Good Processability
- Lubricated
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Processing Information (Injection Molding)
- Impact Properties
- Hardness
Value | Units | Test Method / Conditions | |
Density | 1.31 | — | ASTM D792 |
Density | 1.31 | — | ISO 1183 |
Specific Gravity | 1.31 | — | ISO 1183 |
Specific Gravity | 1.31 | — | ASTM D792 |
Melt Mass Flow Rate (at 250°C, 2.16 kg) | 12 - 25 | g/10 min | ASTM D1238 |
Molding Shrinkage (at 0.125 in, Flow) | 0.016 - 0.022 | in/in | ASTM D955 |
Water Absorption (24 hrs) | 0.08 | % | ASTM D570 |
Water Absorption (at Equilibrium, 73°F) | 0.34 | % | ASTM D570 |
Value | Units | Test Method / Conditions | |
Tensile Strength (at Yield, 0.125 in) | 7500 | psi | ASTM D638 |
Tensile Strength (at Break, 0.125 in) | 7500 | psi | ASTM D638 |
Tensile Elongation (at Yield, 0.125 in) | 3.5 | % | ASTM D638 |
Tensile Elongation (at Break, 0.125 in) | 200 | % | ASTM D638 |
Flexural Modulus (at 0.125 in) | 335000 | psi | ASTM D790 |
Flexural Strength (at 0.125 in) | 11500 | psi | ASTM D790 |
Value | Units | Test Method / Conditions | |
Deflection Temperature Under Load (at 66 psi, 0.125 in, Unannealed) | 300 | °F | ASTM D648 |
Deflection Temperature Under Load (at 264 psi, 0.125 in, Unannealed) | 127 | °F | ASTM D648 |
Vicat Softening Temperature | 374 | °F | ISO 306/B50 |
Value | Units | Test Method / Conditions | |
Volume Resistivity | 10000000000000000 | ohms·cm | ASTM D257 |
Dielectric Strength (at 0.0625 in, in Oil) | 580 | V/mil | ASTM D149 |
Dielectric Strength (at 0.125 in, in Air) | 390 | V/mil | ASTM D149 |
Dielectric Strength (at 0.125 in, in Oil) | 390 | V/mil | ASTM D149 |
Dielectric Constant (at 100 Hz) | 3.3 | — | ASTM D150 |
Dielectric Constant (at 1 MHz) | 3.1 | — | ASTM D150 |
Dissipation Factor (at 100 Hz) | 0.002 | — | ASTM D150 |
Dissipation Factor (at 1 MHz) | 0.02 | — | ASTM D150 |
Value | Units | Test Method / Conditions | |
Drying Temperature | 240 - 250 | °F | — |
Drying Time | 3.0 - 4.0 | hr | — |
Front Temperature | 470 - 500 | °F | — |
Middle Temperature | 460 - 490 | °F | — |
Mold Temperature | 110 - 170 | °F | — |
Rear Temperature | 450 - 480 | °F | — |
Maximum Drying Time | 8 | hr | — |
Processing Temperature (Melt) | 450 - 500 | °F | — |
Value | Units | Test Method / Conditions | |
Impact Strength (at 73°F, Notched Charpy) | 2.5 | ft·lb/in² | ISO 179/1eA |
Impact Strength (at 73°F, 0.125 in, Notched Izod) | 1 | ft·lb/in | ASTM D256 |
Impact Strength (at 73°F, Notched Izod) | 2.2 | ft·lb/in² | ISO 180/1A |
Impact Strength (at 73°F, 0.125 in, Unnotched Izod) | 30 | ft·lb/in | ASTM D4812 |
Gardner Impact Strength (at 0.125 in) | 320 | in·lb | ASTM D3029 |
Value | Units | Test Method / Conditions | |
Rockwell Hardness (R-Scale) | 117 | — | ASTM D785 |
Rockwell Hardness (M-Scale) | 78 | — | ISO 2039-2 |
Regulatory & Compliance
- Certifications & Compliance
- Agency Ratings & Compliance
RoHS Compliant
Packaging & Availability
- Regional Availability
- Availability
North America