Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Product Highlights
- Low exothermic peak
- Preaccelerated
- Thixotropic
- With catalyst indicator
Applications & Uses
- Applications
- Application Method
- Composites Processing Methods
Properties
- Color
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Specific weight at 20°C | 11, 1 | g/cm3 | — |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 460 - 620 | mPa.s | MT-CUT25V |
| Solid Content | 58 - 62 | % | MT-CU001C |
| Gel Time at 20°C + 1,5% MEKP50 | 18 - 26 | minutes | RS.08.G |
| Delta at 20°C + 1,5% MEKP50 | 16 - 24 | minutes | RS.08.G |
| Exothermic peak at 20°C + 1,5% MEKP50 | 130 - 160 | °C | RS.08.G |
| Value | Units | Test Method / Conditions | |
| Elongation at break at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 1, 7 | % | ISO 527 (2012) |
| Tensile strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 50 | MPa | ISO 527 (2012) |
| Tensile Modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3600 | MPa | ISO 527 (2012) |
| Flexural strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 95 | MPa | ISO 178/B (2010) |
| Flexural modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3400 | MPa | ISO 178/B (2010) |
| HDT at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 75 | °C | ISO 75 -2A (2013) |
| Barcol Hardness at 25°C at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 40 | — | ASTM D 2583 (2007) |
Storage & Handling
- Shelf Life
- 3 Months (23°C in Dark )
- Handling and Storage
Store in the shade, out of direct sunlight. Keep storage temperature below 25°C. Unseal container just before use. Shelflife will be reduced reaching higher temperature.