Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Product Highlights
- Preaccelerated
Applications & Uses
- Markets
- Applications
Properties
- Color
- Typical Properties
- Cured Properties
Value | Units | Test Method / Conditions | |
Specific weight at 20°C | 1, 12 | g/cm3 | — |
Exothermic peak at 20°C + 1,5% MEKP50 | 150 - 180 | °C | RS.08.G |
Brookfield Viscosity at 25°C, sp 2 rpm 20 | 650 - 850 | mPa.s | MT-CUT25V |
Solid Content | 67 - 71 | % | MT-CU001C |
Gel Time at 20°C + 1,5% MEKP50 | 8:30 - 9:30 | minutes | RS.08.G |
Delta at 20°C + 1,5% MEKP50 | 9-13 | minutes | RS.08.G |
Value | Units | Test Method / Conditions | |
Elongation at break at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 2, 5 | % | ISO 527 (2012) |
Tensile strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 60 | MPa | ISO 527 (2012) |
Flexural strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 115 | MPa | ISO 178/B (2010) |
Tensile Modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3400 | MPa | ISO 527 (2012) |
Flexural modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3300 | MPa | ISO 178/B (2010) |
HDT at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 100 | °C | ISO 75 -2A (2013) |
Glass transition at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 110 | °C | ASTM E 1545 (2011) |
Barcol Hardness at 25°C at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 43 | — | ASTM D 2583 (2007) |
Storage & Handling
- Shelf Life
- 4 Months (23°C in Dark )