Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Composite Materials Functions
- Technologies
- Product Families
Features & Benefits
- Product Highlights
- Low styrene emission
- Low styrene content
- With catalyst indicator
- Preaccelerated
- Thixotropic
Applications & Uses
- Markets
- Application Method
- Composites Processing Methods
Properties
- Color
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Specific weight at 20°C | 1, 11 | g/cm3 | — |
| Exothermic peak at 20°C + 1,5% MEKP50 | 165 - 195 | °C | RS.08.G |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 750 - 960 | mPa.s | MT-CUT25V |
| Solid Content | min. 65 | % | MT-CU001C |
| Gel Time at 20°C + 1,5% MEKP50 | 28 - 36 | minutes | RS.08.G |
| Delta at 20°C + 1,5% MEKP50 | 10-17 | minutes | RS.08.G |
| Value | Units | Test Method / Conditions | |
| Flexural modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3400 | MPa | ISO 178/B (2010) |
| Tensile strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 55 | MPa | ISO 527 (2012) |
| Tensile Modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 3500 | MPa | ISO 527 (2012) |
| Flexural strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 105 | MPa | ISO 178/B (2010) |
| HDT at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 67 | °C | ISO 75 -2A (2013) |
| Barcol Hardness at 25°C at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 37 | — | ASTM D 2583 (2007) |
| Elongation at break at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C | 2, 0 | % | ISO 527 (2012) |
Safety & Health
- Product Safety
Stir the resin before use, without use air bubbles, As the resin includes a film-forming agent, we recommend that the laminate should first rubbed down before bonding or relaminating.
Storage & Handling
- Shelf Life
- 3 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature