DISTITRON - 1402 AST - Polynt - Polyester - Polyesters

Identification & Functionality

Features & Benefits

Materials Features: Good UV Protection
Product Highlights: Paraffinated

Preaccelerated

Light stabilized

Thixotropic

Applications & Uses

Markets: Building & Construction,
Industrial
Applications: Building & Construction — Building Envelope & Roofing
Glazing & Window Elements,
Shingles & Tiles
Building & Construction — Building Materials
Fence, Decks & Rails,
Interior Fixtures,
Pipes & Plumbing,
Siding & Trim,
Structural Components,
Wall Panels
Industrial — Chemical & Industrial Manufacturing
Equipment & Parts
Building & Construction — Infrastructure, Roads & Paving
Pavement, Highways, Roads & Bridges
Industrial — Oil, Gas & Mining
Refining & Gas Processing
Industrial — Power, Water & Utilities
Power & Utilities,
Renewable Energy
Application Method: Spray
Composites End Use: Pipes,
Tanks
Composites Processing Methods: Hand Lay-up,
Spray Lay-up

Properties

	Value	Units	Test Method / Conditions
Specific weight at 20°C	1, 11	g/cm3	—
Solid Content	58 - 62	%	MT-CU001C
Exothermic peak at 20°C + 1,5% MEKP50	170 - 200	°C	RS.08.G
Brookfield Viscosity at 25°C, sp 2 rpm 20	470 - 650	mPa.s	MT-CUT25V
Gel Time at 20°C + 1,5% MEKP50	15 - 20	minutes	RS.08.G
Delta at 20°C + 1,5% MEKP50	8 - 14	minutes	RS.08.G

	Value	Units	Test Method / Conditions
Elongation at break at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C	1, 4	%	ISO 527 (2012)
Tensile strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C	50	MPa	ISO 527 (2012)
HDT at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C	75	°C	ISO 75 -2A (2013)
Flexural strength at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C	105	MPa	ISO 178/B (2010)
Tensile Modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C	4000	MPa	ISO 527 (2012)
Flexural modulus at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C	3800	MPa	ISO 178/B (2010)
Glass transition at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C	90	°C	ASTM E 1545 (2011)
Barcol Hardness at 25°C at 23°C for 24h/ + 2h at 100°C /+ 1h at 100°C	45	—	ASTM D 2583 (2007)

Safety & Health

Product Safety: Stir the resin before use, without use air bubbles, As the resin includes a film-forming agent, we recommend that the laminate should first rubbed down before bonding or relaminating.

Storage & Handling

Shelf Life: 3 Months (23°C in Dark )
Handling and Storage: Store in the shade, out of direct sunlight

Keep storage temperature below 25°C

Unseal container just before use

Shelf life will be reduced reaching higher temperature

DISTITRON® 1402 AST