- Clear unaccelerated
- Type 1140 (DIN 16946-2)
- Type UP 2 (DIN 18820-1)
Applications & Uses
- Applications
- Composites Processing Methods
Properties
- Color
- Typical Properties
- Cured Properties
| Value | Units | Test Method / Conditions | |
| Specific weight at 20°C | 1, 11 | g/cm3 | — |
| Exothermic peak at 20°C + 1,5% MEKP50 | 185 - 215 | °C | RS.08.G |
| Acidity at 20°C + 1,5% MEKP50 | 11-18 | mg KOH/g | MT-CU001I |
| Solid Content | 61 - 65 | % | MT-CU001C |
| Brookfield Viscosity at 25°C, sp 2 rpm 20 | 470 - 630 | mPa.s | MT-CUT25V |
| Gel Time at 20°C + 1,5% MEKP50 | 24 - 31 | minutes | RS.08.G |
| Delta at 20°C + 1,5% MEKP50 | 7-13 | minutes | RS.08.G |
| Value | Units | Test Method / Conditions | |
| Barcol Hardness at 25°C at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 44 | — | ASTM D 2583 (2007) |
| Tensile Modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3700 | MPa | ISO 527 (2012) |
| Flexural modulus at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3600 | MPa | ISO 178/B (2010) |
| Tensile strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 80 | MPa | ISO 527 (2012) |
| Flexural strength at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 145 | MPa | ISO 178/B (2010) |
| HDT at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 94 | °C | ISO 75 -2A (2013) |
| Elongation at break at 23°C for 24h /+ 2h at 100°C /+ 1h at 100°C | 3,5 | % | ISO 527 (2012) |
Storage & Handling
- Shelf Life
- 3 Months (23°C in Dark )
- Handling and Storage
- Store in the shade, out of direct sunlight
- Keep storage temperature below 25°C
- Unseal container just before use
- Shelf life will be reduced reaching higher temperature